研究了温度对PVC断裂伸长率、拉伸强度及加热形变量(针入度)的影响,发现与未增塑PVC相类似,增塑PVC在90 ℃左右出现断裂伸长率最大值;增塑PVC的形变量随PVC聚合度(结晶度)的增加而减小,软化温度则上升.对于退火处理的增塑PVC,形变在退火温度所对应的重结晶熔融温度范围出现转折.认为以上实验结果与增塑PVC中微晶交联网络结构的存在及其在升温条件下的破坏有关,提出了增塑PVC的微晶交联结构物理模型.根据经典的橡胶弹性理论,计算了交联网络中交联点之间平均分子量(c),发现c随PVC聚合度(结晶度)的增加而减小.
参考文献
| [1] | Alfray T et al.[J].Industrial and Engineering Chemistry,1949,41:701. |
| [2] | Acosta R A et al.[J].Polymeric Preprints(American Chemical Society Division of Polymer Chemistry),1971,12:745. |
| [3] | Nakajima A et al.[J].Journal of Macromolecular Sciences:Physics,1981,20(02):257. |
| [4] | Iobst S A et al.[J].Polymeric Preprints(American Chemical Society Division of Polymer Chemistry),1970,12:765. |
| [5] | Patterson K G et al.[J].Colloid and Polymer Science,1982,260(09):851. |
| [6] | 黄志明,包永忠,翁志学.聚氯乙烯结晶行为研究[J].高分子材料科学与工程,1998(04):78-81. |
| [7] | Pinner S H .[Z].Plastics,1965. |
| [8] | De VRIES A J;Bonnebat C .[J].Polymer Engineering and Science,1976,16:93. |
| [9] | Brown H R et al.[J].Polymer,1982,230:1508. |
| [10] | Peppas N A;Merrill E W .[J].Journal of Applied Polymer Science,1977,21:1763. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%