采用模压方法制备了多元PEEK耐磨汽车材料.用环-块磨损实验机对复合材料进行了磨损试验,用SEM方法对复合材料的磨损表面进行了观察和分析,并利用DSC、FT-IR和SEM分析方法对复合材料的磨屑进行了研究,在上述基础上进行了复合材料的磨损机理探讨.结果表明,与PEEK相比,PEEK复合材料具有优良的摩擦学性能;PEEK复合材料磨屑的熔点比相应模压材料有所降低,且磨屑的熔限比相应的模压材料有所加宽;随着Ekonol含量的增加,复合材料的磨损机理发生了由粘着磨损为主向疲劳磨损为主的转变.
参考文献
| [1] | Corvelli A A;Biermann P J;Roberts J C.[J].Bioengineering Division (Publication)BED,1997(36):313. |
| [2] | Wang A.;Stark C.;Dumbleton J.H.;Lin R. .Suitability and limitations of carbon fiber reinforced PEEK composites as bearing surfaces for total joint replacements[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(2):724-727. |
| [3] | Wang Q H;Xue Q J;Liu W M .[J].Wear,2000,243(01):140. |
| [4] | 龙春光,张厚安.Ekonol/G/MoS2/PEEK复合材料的力学性能[J].功能材料,2003(05):589-591. |
| [5] | 蹇锡高;刘少琼 .[J].塑料加工,1999,27(03):36. |
| [6] | Yu L G;Yang S R;Liu Wei M et al.[J].Journal of Applied Polymer Science,2000,76(02):179-184. |
| [7] | 龙春光,戴文利,陈平.聚醚醚酮复合材料的转移膜研究[J].润滑与密封,2005(03):16-19. |
| [8] | 章明秋;张志毅 .[J].摩擦学学报,1996,16(03):226. |
| [9] | 张人佶,冯显灿.聚醚醚酮及其复合材料的摩擦学研究进展[J].材料研究学报,2002(01):1-8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%