In the present study, titania coatings were prepared under different current density conditions in micro-arc oxidation (MAO) process on titanium alloy in NaAlO2 solution. The aim of this work was to study the effects of current density on the microstructure of titania coatings. The morphology and phase composition of the coatings were investigated by field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD) and Raman spectra. The thickness and surface roughness of the coatings were characterized by confocal laser Scanning Microscopy (CLSM). The results showed that the coatings were composed of crystalline anatase and rutile phases of TiO2, and contain a network of evenly distributed small pores. It has also shown that an increase in current density leads to an increase in rutile content.
参考文献
| [1] | J.-z. Chen;Y.-l. Shi;L. Wang .Preparation and properties of hydroxyapatite-containing titania coating by micro-arc oxidation[J].Materials Letters,2006(20):2538-2543. |
| [2] | X. Nie;A. Leyland;A. Matthews .Deposition of layered bioceramic hydroxyapatite/TiO{sub}2 coatings on titanium alloys using a hybrid technique of micro-arc oxidation and electrophoresis[J].Surface & Coatings Technology,2000(1/3):407-414. |
| [3] | A. L. Yerokhin;X. Nie;A. Leyland;A. Matthews .Characterisation of oxide films produced by plasma electrolytic oxidation of a Ti-6Al-4V alloy[J].Surface & Coatings Technology,2000(2/3):195-206. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%