以正硅酸乙酯(TEOS)和水合硝酸铝(ANN)为原料,采用溶胶-凝胶法合成了无定形Al2O3-2SiO2粉体.通过XRD与FT-IR对其无定形相结构进行了表征,发现其结构与偏高岭士相似.为了考察粉体的碱激发活性,用SiO2/Na2O摩尔比为1.2的硅酸钠溶液对其进行碱激发试验,结果表明合成的无定形Al2O3-2SiO2粉体具有碱激活性,3 d抗压强度达到24MPa.
参考文献
| [1] | Davidovits J .[P].US Patent,4349386,1982. |
| [2] | Davidovits J .[P].US Patent,4472199,1984. |
| [3] | Palomo A;Blancovarela M T;Granizo M L et al.[J].Cement and Concrete Research,1999,29:997. |
| [4] | Phair J W;Smith J D;Van Deventer J S J .[J].Materials Letters,2003,57:4356. |
| [5] | 王建,董家禄,刘杨,须沁华.偏高岭土合成4A沸石机理的研究[J].无机化学学报,2000(01):31-36. |
| [6] | Madani A;Aznar A;Sanz J et al.[J].Journal of Physical Chemistry,1990,94:760. |
| [7] | Rahier H.;Vanmele B.;Biesemans M.;Simons W. .LOW-TEMPERATURE SYNTHESIZED ALUMINOSILICATE GLASSES .3. INFLUENCE OF THE COMPOSITION OF THE SILICATE SOLUTION ON PRODUCTION, STRUCTURE AND PROPERTIES[J].Journal of Materials Science,1997(9):2237-2247. |
| [8] | 李克亮;Huang Guohong;黄国泓;王冬 et al.[J].水泥,2005,11:49. |
| [9] | 罗永康,马智,吴杰,齐晓周.煅烧温度对高岭土结构及其氧化铝浸出率的影响[J].化学工业与工程,2005(04):263-266. |
| [10] | 王雪静,周继红,黄浪,方克明.苏州高岭土在不同温度煅烧时的产物[J].北京科技大学学报,2006(01):59-62. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%