A hot-rolled deep drawing (HDD) steel with high r-value and uniform distribution of{ 111} texture in thickness was developed by hot rolling in ferrite region with lubricatingbetween the roller and the steel. The experimental results show that the carbon contentand finish rolling temperature have significant effects on beneficial texture {111}, andlubricating during hot rolling at low temperature in α-region makes the distributionof the texture uniform. Three basic requirements needed to meet for HDD steel wereconcluded by comparing different carbon contents and hot rolling processes.
参考文献
| [1] | S Matsuoka;K Sakata;O Furukimi.[A].Aachen,Germany,1991:85. |
| [2] | K Tsunoyama.[A].The Minerials,Metals & Materials Society,USA,1998:27. |
| [3] | X J Wang;Y W Ma;Y L Kang.[A].Aachen,Germany,1998:27. |
| [4] | Y L Kang.Quality Controlling and Formability of Modern Automobile Steel Sheets[M].北京:冶金工业出版社,1999:44. |
| [5] | R Seabald;B Beckers;G Gottstein.[A].Aachen,Germany,1998:363. |
| [6] | X J Wang;D L Cui;D Tang .[J].Iron and Steel,1990,25(06):61. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%