Combustion reaction welding, one promising method to weld ceramics and metals, was used to weld TiB2 and Mo. The results showed that the reacted products through combustion reaction were TiB2 and MoB when the Mo contents in reactants were 20 wt pct and 40 wt pct while there was Mo besides MoB and TiB2 when there were 60 wt pct and 80 wt pct Mo in reactants. Diffusion of elements occurred at the interfaces of the two substrates. The interfaces between the reacted and the two substrates were indistinct after being welded. The welding temperature strongly affected properties of the samples. The value of bending strength of the sample with 80 wt pct Mo in reactant welded at 1500℃ was the highest, 368.52 MPa. The highest value of shear strength among all the samples was that of the one with 40 wt pct Mo in reactant welded at 1500℃, 50.97 MPa.
参考文献
| [1] | RunzhangYUAN;Zhengyi FU;Weimin WANG .[J].Propag High-Temp Synth,2001,4(10):435. |
| [2] | HaoWANG;Zhengyi FU;Weimin WANG;Runzhang YUAN .[J].Chinese Journal of Nonfer Metals,1998,8(04):313. |
| [3] | Jcasting;P Costa.Boron and Refractory Borides[M].Springer-VerlagPressBerlin,1977:457. |
| [4] | YuchengWANG;ZhengyiFU .[J].复合材料学报,2002,19:50. |
| [5] | MGNicholas;D A Mortimer .[J].Materials Science and Technology,1985,1:657. |
| [6] | MTurwitt.Joining Ceramics[J].Glass and Metal Diisseldorf DVS-Verlag GmbH,1997 |
| [7] | Huaping Xiong .Effect of Metallurgical Behaviour at the Interface between Ceramic and Interlayer on the Si_3N_4/1.25Cr-0.5Mo Steel Joint Strength[J].Journal of Materials Science & Technology,1998(1):20-24. |
| [8] | WRoertandJrMessler .[J].Current Advances in Materials and Processes,1995,147:47. |
| [9] | RWJRMessler;M A Zurbuchen;T T Orling .[J].Welding Journal,1995,10:37. |
| [10] | YoshinariMiyamoto.[J].Journal of Materials Research,1986(01):7. |
| [11] | RWJRMesslerandTTOrling .[J].Current Advances in Materials and Processes,1995,6:2. |
| [12] | ZJSheng .[J].Journal of Mater Rev,2000,14:67. |
| [13] | D. H. He;Z. Y. Fu;J. Y. Zhang;Q. J. Zhang .Welding TiB_2 and Fe with Combustion Synthesis[J].Key engineering materials,2003(249):115-118. |
| [14] | Jinyong ZHANG,Zhengyi FU,Weiming WANG,Hao WANG.Microstructure and Mechanical Properties of TiB2/(Ni+Mo) Composites Fabricated by Hot Pressing[J].材料科学技术学报(英文版),2000(06):634-636. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%