以 Mo2C/VC 作为质子交换膜燃料电池氧还原催化剂, 并采用单电池和电化学循环伏安扫描技术考察了其氧还原活性,同时结合 X 射线衍射和 X 射线光电子能谱对其电催化机理进行初步分析. 结果表明, Mo2C/VC 对氧还原也具有电催化活性, 在 0.34, 0.45 和 0.55 V 处出现三对可逆的氧化还原峰. Mo2C/VC 的体相为β-Mo2C, 表相为+δ价(5 ≤δ≤ 6)的 MoOxCy 和 MoOz. Mo2C/VC 的电催化性能可能是由于其表面钝化物种(MoOxCy 和 MoOz)的氧化还原, 以及氧在 Mo2C 晶格中的迁入和迁出引起的.
参考文献
| [1] | Li Y J;Chang C C;Wen T C .[J].Journal of Applied Electrochemistry,1997,27:227. |
| [2] | Min M K;Cho J;Cho K;Kim H .[J].Electrochimica Acta,2000,45:4211. |
| [3] | Toda T;Igarashi H;Uchida H;Watanabe M .[J].Journal of the Electrochemical Society,1999,146:3750. |
| [4] | Tamizhmani G;Capuano G A .[J].Journal of the Electrochemical Society,1994,141:968. |
| [5] | Levy R B;Boudart M .[J].Science,1973,181:547. |
| [6] | McIntyre D R;Burstein G T;Vossen A .[J].Journal of Power Sources,2002,107:67. |
| [7] | Oyama S T;Schlatter J C;Motcalfe III J E;Lambert J M Jr .[J].Industrial and Engineering Chemistry Research,1988,27:1639. |
| [8] | Zhang D Y;Ma Z F;Wang G X;Konstantinov K Yuan X X Liu H K .[J].Electrochemical and Solid-State Letters,2006,9:A423. |
| [9] | Bronoel G;Museux E;Leclercq G;Leclercq L Tassin N .[J].Electrochimica Acta,1991,36:1543. |
| [10] | Matsumoto T;Nagashima Y;Yamazaki T;Nakamura J .[J].Electrochemical and Solid-State Letters,2006,9:A160. |
| [11] | 位辰先,田建华,梁宝臣,刘邦卫.制备条件对卟啉钴氧还原催化性能的影响[J].天津理工学院学报,2004(03):38-40. |
| [12] | Zhong H;Zhang H;Liu G;Liang Y Hu J Yi B .[J].Electrochemistry Communications,2006,8:707. |
| [13] | Izhar S;Yoshida M;Nagai M .[J].Electrochimica Acta,2009,54:1255. |
| [14] | 靳广洲,樊秀菊,孙桂大,高俊斌,朱建华.碳化钼的制备与表征[J].无机材料学报,2007(03):504-508. |
| [15] | Perez-Romo P;Potvin C;Manoli J M;Chehimi M M Dj'ega-Mariadassou G .[J].Journal of Catalysis,2002,208:187. |
| [16] | Delporte P;Meunier F;Pham-Huu C;Vennegues P Ledoux M J Guille J .[J].Catalysis Today,1995,23:251. |
| [17] | 田立朋,李伟善,李红.Pt/HxMoO3电极上甲醇的催化氧化[J].精细化工,2000(Z1):107-110. |
| [18] | 邓选英,章冬云,王昕,原鲜霞,马紫峰.碳纳米管负载金属卟啉电催化剂制备及其催化活性[J].催化学报,2008(06):519-523. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%