The effect of manganese on the as-cast structure and hardening behavior of high chromium white cast iron subjected to sub-critical treatment was studied. The results indicate that the fraction of retained austenite and the manganese distribution in as-cast alloys are controlled by manganese content. The manganese distribution in as-cast alloys is not homogeneous. The manganese content in carbide is higher than that in matrix. Whether the secondary hardening occurs or not and the peak hardness of secondary hardening is controlled by manganese content in retained austenite in as-cast structure. Higher manganese content can cause more retained austenite. The secondary hardening occurs in sub-critical treating process if the fraction of retained austenite is high.
参考文献
| [1] | Tabrett C P;Sare I R .The Effect of Heat Treatment on the Abrasion Resistance of Alloy White Iron[J].Wear,1997,203-204:206-219. |
| [2] | Hann SK.;Gates JD. .A TRANSFORMATION TOUGHENING WHITE CAST IRON[J].Journal of Materials Science,1997(5):1249-1259. |
| [3] | Powell GLF.;Bee JV. .SECONDARY CARBIDE PRECIPITATION IN AN 18 WT-PERCENT CR-1 WT-PERCENT MO WHITE IRON[J].Journal of Materials Science,1996(3):707-711. |
| [4] | 段汉桥.锰对高铬铸铁凝固过程和组织的影响[J].热加工工艺,2001(03):23-25. |
| [5] | Kim C .[J].Journal of Heat Treating,1979,1(02):43-45. |
| [6] | HAO Shi-jian.High Chromium Abrasion Resistance Cast Iron[M].北京:煤炭工业出版社,1992 |
| [7] | 孙志平,沈保罗,高升吉,王均,黄四九.亚临界热处理对高铬白口铸铁组织和耐磨性的影响[J].材料热处理学报,2003(03):54-57. |