采用氧化物陶瓷工艺制备了高磁导率低损耗锰锌铁氧体材料,研究了Nb2O5掺杂对材料磁性能的影响。结果表明掺杂0.015%（质量分数）Nb2O5的锰锌铁氧体材料具有较好的磁性能：起始磁导率μi=13386,起始磁导率比温度系数αμ/μi=-0.6×10-6/K,相对损耗因数tanδ/μi=3.2×10-6。
Mn-Zn ferrite materials with high initial permeability and low specific loss factor were prepared by the conventional ceramic technology.The effects of Nb2O5 dopant on the magnetic properties were researched.The results showed that Mn-Zn ferrite,which was doped with 0.015wt% Nb2O5,had a good soft magnetic property with the initial permeability μi=13386,the specific temperature factor of initial permeability αμ/μi=-0.6×10-6/K and the specific loss factor tanδ/μi=3.2×10-6.
参考文献
| [1] | Hessien, MM;Rashad, MM;El-Barawy, K;Ibrahim, IA .Influence of manganese substitution and annealing temperature on the formation, microstructure and magnetic properties of Mn-Zn ferrites[J].Journal of Magnetism and Magnetic Materials,2008(9):1615-1621. |
| [2] | 戴煜辉,尉旭波,苏桦,张怀武.P2O5掺杂对高磁导率MnZn铁氧体性能的影响[J].磁性材料及器件,2005(02):29-30. |
| [3] | Yu Z;Sun K;Li LH;Liu YF;Lan ZW;Zhang HW .Influences of Bi2O3 on microstructure and magnetic properties of MnZn ferrite[J].Journal of Magnetism and Magnetic Materials,2008(6):919-923. |
| [4] | Son S.;Swaminathan R.;McHenry ME. .Structure and magnetic properties of rf thermally plasma synthesized Mn and Mn-Zn ferrite nanoparticles[J].Journal of Applied Physics,2003(10 Pt.2):7495-7497. |
| [5] | Zaspalis VT.;Antoniadis E.;Papazoglou E.;Tsakaloudi V.;Nalbandian L. Sikalidis CA. .The effect of Nb2O5 dopant on the structural and magnetic properties of MnZn-ferrites[J].Journal of Magnetism and Magnetic Materials,2002(1/3):98-109. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%