Modified TiO2 films have been prepared by combining commercial titania powders (Degussa P25) with sol-gel made by titanium chloride (Ti-sol). The result shows that clusters are formed by nanoparticles and large pores can be seen on the surface of the TiO2 films. The short circuit photocurrent density and photoelectric conversion efficiency of the solar cells are obviously enhanced compared with those without modification. The relationship between the photoelectric conversion efficiency and the amount of Ti-sol was investigated. With the addition of 30 wt% Ti-sol, the photoelectric conversion efficiency as high as 9.75% is achieved, increasing by 28.3% compared with the solar cells without modification.
参考文献
| [1] | |
| [2] | B. O0Regan and M. Gratzel: Nature, 1991, 353, 737.[2 ] M.K. Nazeeruddin, A. Kay, I. Rodicio, R. Humphry, E. Muller, P. Liska, N. Vlachopoulos and M. Gratzel: J. Am. Chem. Soc., 1993, 115, 6382.[3 ] S. Ito, P. Chen, P. Comte, M.K. Nazeeruddin, P. Liska, P. Pechy and M. Gratzel: Prog. Photovolt-Res. Appl., 2007, 15, 603.[4 ] Y.J. Chen, E. Stathatos and D.D. Dionysiou: J. Photochem. Photobiol. A-Chem., 2009, 203, 192.[5 ] X.B. Chen and S.S. Mao: Chem. Rev., 2007, 107, 2891.[6 ] S. Ngamsinlapasathian, T. Sreethawong, Y. Suzuki and S. Yoshikawa: Sol. Energy Mater. Sol. Cells, 2005, 86, 269.[7 ] K. Kajihara and T. Yao: J. Sol-gel Sci. Technol., 2000, 17, 173.[8 ] L.H. Hu, S.Y. Dai, J. Weng, S.F. Xiao, Y.F. Sui, Y. Huang, S.H. Chen, F.T. Kong, X. Pan, L.Y. Liang and K.J. Wang: J. Phys. Chem. B, 2007, 111, 358.[9 ] E.V. Skorb, L.I. Antonouskaya, N.A. Belyasova, D.G. Shchukin, H. MÄ |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%