以生物活性玻璃粉末SiO2-CaO-P2O5系统玻璃、β-TCP和磷酸铵调和液均匀混合制得多孔玻璃基骨水泥,利用XRD、FTIR和SEM对多孔骨水泥的晶相、化学组成和显微结构进行了观察和分析,并对其显气孔率进行了测试.实验结果表明,随着浸泡时间的增加,β-TCP促进了HAP晶体的生成和完善,HAP晶体呈短柱状,交织分布于玻璃颗粒间隙,尺寸大约为200nm.对试样显气孔率测试结果表明,β-TCP的降解显著增加了骨水泥的显气孔率,并且随着β-TCP含量的增加而增加.
参考文献
| [1] | Freeman M A R;Bradlay G M;Ravell R A .[J].Journal of Bone and Joint Surgery-British Volume,1982,64(03):489-493. |
| [2] | Saha S;Pal S .[J].Journal of Biomedical Materials Research,1984,18(03):435-462. |
| [3] | Malony W J;Jasty M;Rosemberg A et al.[J].Journal of Bone and Joint Surgery-British Volume,1990,72(05):966-970. |
| [4] | Brown W E;Chow L C.A New Calcium Phosphate Water Setting Cement[A].Westerville:American Ceramic Society,1986:352-379. |
| [5] | Chow L C;Talegi S;Constantino P D;Friedman C D et al.[J].Materials Research Society Symposium Proceedings,1991,179(01):3-24. |
| [6] | Shindo M L;Constantino P D;Friedman C D et al.[J].Archives of Otolaryngology Head and Neck Surgery,1993,119(02):185-190. |
| [7] | 周萘,黄文,张娟,姚维芳.玻璃基生物水泥的结构研究[J].玻璃与搪瓷,2001(03):24-26,19. |
| [8] | 付强,周萘,黄文旵,王德平,张丽英.玻璃基生物骨水泥内部纳米羟基磷灰石的形成研究[J].功能材料,2004(03):376-378,382. |
| [9] | 戴红莲,李世普,闫玉华,李小溪,沈春华.β-磷酸三钙多孔生物陶瓷植入体内后的组成变化[J].硅酸盐学报,2004(07):800-807. |
| [10] | 李世普;冯凌云;贾莉 .[J].磷酸盐工业,1995,12:146-148. |
| [11] | Napper D H .[J].Journal of Colloid and Interface Science,1970,33(03):384-392. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%