采用RF磁控溅射技术,通过改变溅射时间的方式在丝织物基材上沉积纳米银薄膜.采用SEM和AFM对丝纤维表面银薄膜进行表征.采用剥离试验讨论薄膜与丝织物基材间的界面结合.结果表明,随溅射时间的延长,丝纤维表面纳米银逐渐增加,纳米银粒径呈增大趋势,薄膜逐渐向连续结构过渡.在实验范围内,溅射时间延长,薄膜与基材间的结合牢度得到提高.
参考文献
| [1] | Banchi L.New trends in technical textiles[J].Rivista Della Teehn,2001(03):62. |
| [2] | Dowling DP.;Betts AJ.;Pope C.;McConnell ML.;Eloy R.;Arnaud MN. .Anti-bacterial silver coatings exhibiting enhanced activity through the addition of platinum[J].Surface & Coatings Technology,2003(0):637-640. |
| [3] | Hum A P J .Fabric area network--A new wireless communications infrastructure to enable ubiquitous networking and sensing on intelligent clothing[J].Computer Networks,2001,35:391. |
| [4] | 洪剑寒,王鸿博,魏取福.氩气压强对PET基磁控溅射银膜结构及导电性能的影响[J].材料导报,2006(z2):83-85. |
| [5] | 洪剑寒,王鸿博,魏取福,高卫东.磁控溅射法制备纳米Ag薄膜的AFM分析和导电性能[J].纺织学报,2006(09):14-17. |
| [6] | 洪剑寒,王鸿博.非织造布磁控溅射镀银的导电和抗紫外性能[J].印染,2008(06):10-11,35. |
| [7] | 陈萌,罗世永,许文才.纳米银制备及其在抗菌包装和印刷中的应用[J].包装工程,2009(05):90-92,95. |
| [8] | Kurt H Stem.Metallurgical and ceramic protective coating[M].London:Chaopman&Hall,1996:306. |
| [9] | 周志华,傅明喜,黄兴民,陆琼晔.磁控溅射工艺参数对不锈钢薄膜结合性能的影响[J].材料保护,2004(11):27-28,62. |
| [10] | 顾剑锋;周平南;杨晓豫.离子束增强沉积TiN薄膜界面结合强度的研究[J].金属热处理学报,1997(06):30. |
| [11] | 鲍祖本.MCP薄膜生产工艺对镀铝后铝层附着牢度的影响分析[J].真空,2008(02):64-66. |
| [12] | 黄晓辉,左秀荣,王齐伟,李勇.铝表面磁控溅射沉积不锈钢薄膜及其性能[J].特种铸造及有色合金,2009(08):770-773. |
| [13] | 邓炳耀,刘江峰,魏取福,高卫东,晏雄.纤维基纳米结构材料的界面性能[J].高分子材料科学与工程,2008(11):79-82. |
| [14] | Wei Qufu;Xu Qiuxiang;Cai Yibing et al.Evaluation of the interfaeial bonding between fibrous substrate and sputter coated copper[J].Surf Coat Teehn,2008,202:4673. |
| [15] | 胡作启;李佐宜;缪向水 等.磁控溅射薄膜的厚度均匀性理论研究[J].华中理工大学学报,1996,24(01):89. |
| [16] | 徐小玉 .射频磁控溅射法制备NiZnCo铁氧体磁性薄膜的微观组织与性能研究[D].江苏大学,2005. |
| [17] | 毛一帆,董树荣.塑料表面溅射电磁屏蔽膜的研究[J].真空,2009(04):24-27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%