The stress relaxation curves of Ultra-Low Carbon Bainitic(ULCB) steels with different Cu and B contents were measured by using Gleeble-1500 dynamic thermal-mechanical simulator. The results show that Cu and B added can accelerate the strain-induced precipitation reaction, and the effect of Cu and B is even more obvious with Cu and B combined addition or Cu content increased. The TEM analysis of precipitate engendered at the temperature of 850℃ C indicate that Nb(C,N) precipitate nucleates dominantly on the dislocation line, and grows with holding time extended while the precipitate particle size increases from 5 nm to 17 nm.