研究了超低碳高铬钢与低碳高铬钢的周期浸润(2％ NaCl水溶液)腐蚀性能和组织形貌,并与工业生产Q235碳钢进行了相应的比较.通过光学显微镜OM、扫描电镜SEM、高分辨透射电镜TEM、XRD射线衍射仪等观察与测试.结果表明:超低碳高铬钢和低碳高铬钢具有优异的耐氯离子腐蚀性能,其腐蚀速率相比Q235分别为21.25％、24.9％,超低碳高铬钢的耐蚀性优于低碳高铬钢,显微组织为板条马氏体和残留奥氏体的高铬钢的耐蚀性优于显微组织为铁素体+珠光体的Q235碳钢.高铬、低碳、马氏体+相间分布的残留奥氏体共同作用提高了高铬钢的耐腐蚀性能.
参考文献
| [1] | M. Kimura;Y. Miyata;Y. Yamane;T. Toyooka;Y. Nakano;F. Murase.Corrosion resistance of high-strength modified 13 % Cr steel[J].Corrosion: The Journal of Science and Engineering,19998(8):756-761. |
| [2] | Y.S. Li;M. Spiegel;S. Shimada.Effect of Al/Si addition on KCI induced corrosion of 9 percent Cr steel[J].Materials Letters,200429(29):3787-3791. |
| [3] | S. Ningshen;M. Sakairi;K. Suzuki.Corrosion Resistance of 9% Cr Oxide Dispersion- Strengthened Steel in Different Electrolytic Media[J].Corrosion: The Journal of Science and Engineering,20139(9):863-874. |
| [4] | 许立宁;朱金阳;谢云;张玉楠;常炜;路民旭.含Cr管线钢的力学性能和耐蚀性能[J].北京科技大学学报,2014(2):200-205. |
| [5] | 梁航;汪兵;刘清友;尚建丽.铁道车辆用3.5％Cr高耐蚀钢组织演变规律研究[J].热加工工艺,2011(24):93-96. |
| [6] | Liu, Ming;Cheng, Xuequn;Li, Xiaogang;Jin, Zhu;Liu, Haixia.Corrosion behavior of Cr modified HRB400 steel rebar in simulated concrete pore solution[J].Construction and Building Materials,2015Sep.15(Sep.15):884-890. |
| [7] | 赵晴;秦勇;朱晓光;冯长杰.马氏体Cr钢亚晶结构的定量表征[J].航空材料学报,2009(6):81-84. |
| [8] | 米丰毅;王向东;汪兵;陈小平;彭云.显微组织对低碳钢耐蚀性的影响[J].中国腐蚀与防护学报,2010(5):391-395. |
| [9] | 晁月林;周玉丽;王全礼;邸全康;王立峰;孙齐松.Cu-P-Cr钢及其焊接接头的周期腐蚀性能[J].材料热处理学报,2015(2):84-90. |
| [10] | 晁月林;周玉丽;邸全康;王立峰;程四华.Cu,P,Cr和Ni对低碳钢耐蚀性的影响[J].中国腐蚀与防护学报,2014(1):70-74. |
| [11] | 孙建波;柳伟;路民旭.成分和组织影响钢CO2腐蚀的研究进展[J].中国腐蚀与防护学报,2008(4):246-250. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%