A sol-gel processing was used to synthesize (Ca0.61,Nd0.26)TiO3 (CNT) nanoparticles doped with Li-Cu-B at low temperature. Orthorhombic perovskite structure phase with a small amount of Li3BO3 secondary phase was formed by calcining the xerogels at 300°C, and monodisperse CNT nano-powders with the grain size of 10−15 nm could be obtained. By using these nanocrystalline CNT powders, dense CNT ceramics could be achieved at the low sintering temperature of 1100°C due to the effect of the small size nanoparticles and liquid phase Li3BO3. And the dielectric properties with dielectric constant (εr= 89.52), quality value factors with frequency (Q£f=17148 GHz) and the temperature coefficient of resonant frequency (τf ) value of +239×10-6/°C were achieved.
参考文献
| [1] | |
| [2] | M.S. Fu, X.Q. Liu and X.M. Chen: J. Eur. Ceram. Soc., 2008, 28, 585.[2 ] M. Yoshida, N. Hara, T. Takada and A. Seki: Jpn. J. Appl. Phys., 1997, 36, 6818.[3 ] M.Z. Hu, H.S. Gu, X.C. Chu, J. Qian and Z.G. Xia: J. Appl. Phys., 2008, 104, 124104.[4 ] H.L. Chen and C.L. Huang: Jpn. J. Appl. Phys., 2002, 41, 5650.[5 ] R. Perla, D.P. Rodney, J.B. Linda and M.T. John: Nature, 2007, 6, 278.[6 ] M. Niederberger, G. Garnweitner, M. Pinna and M. Antonietti: J. Am. Chem. Soc., 2004, 126, 9120.[7 ] A. Kritikaki and A. Tsetsekou: J. Eur. Ceram. Soc., 2009, 29, 1603.[8 ] S.A. Hassanzadeh-Tabrizi and E. Taheri-Nassaj: J. Alloy. Compd., 2010, 464, 289.[9 ] D.D. Khalyavin, A.N. Salak, A.M.R. Senos, P.Q. Mantas and V.M. Ferreira: J. Am. Ceram. Soc., 2006, 89, 1721.[10] J. Park, J. Joo, S.G. Kwon, Y. Jiang and T. Hyeon: Angew. Chem. Int. Edit., 2007, 46, 4630.[11] M. Niederberger: Accounts Chem. Res., 2007, 40, 793.[12] N. Pinna and M. Niederberger: Angew. Chem. Int. Edit., 2008, 47, 5292.[13] G. Garnweitner and M. Niederberger: J. Mater. Chem., 2008, 18, 1171.[14] K.R. Brown and M.J. Natan: Langmuir, 1998, 14, 726.[15] J. Ba, A. Feldhoff, D. Fattakhova-Rohl¯ |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%