直流电弧等离子体喷射法制备自支撑金刚石膜时,电弧区域可分为弧心、弧干和弧边三个区域.本文运用扫描电子显微镜(SEM)、X射线衍射(XRD)、激光Raman光谱、正电子湮没寿命谱(PAL)和力学性能实验机研究了同一块自支撑金刚石膜不同区域的生长面形貌、晶体取向、内应力、空位缺陷和断裂强度.结果表明:随着与直流电弧等离子体弧心距离增加金刚石膜生长更稳定,(220)取向晶粒减少,平均空位缺陷减少,内应力和断裂强度呈现先增大后减小的趋势.
参考文献
| [1] | J. E. Field .ELSI conference: invited lecture liquid impact: theory, experiment, applications[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,1999(0):1-12. |
| [2] | Coe S.E. .Optical, thermal and mechanical properties of CVD diamond[J].Diamond and Related Materials,2000(9-10Sep/Oct):1726-1729. |
| [3] | 王志军,李红莲,董丽芳,李盼来,尚勇.衬底温度对电子辅助增强化学气相沉积金刚石膜的影响[J].人工晶体学报,2008(01):76-82. |
| [4] | 姜春生,郭世斌,刘政,唐伟忠,吕反修.高功率直流电弧等离子体喷射法制备的金刚石厚膜中黑色缺陷的研究[J].人工晶体学报,2009(06):1349-1354. |
| [5] | Lu F.X.;Tang W.Z. .Economical deposition of a large area of high quality diamond film by a high power DC arc plasma jet operating in a gas recycling mode[J].Diamond and Related Materials,1999(9-10):1655-1659. |
| [6] | 刘政 .高功率直流电弧等离子体喷射CVD金刚石膜系统的模拟研究[D].北京科技大学,2009. |
| [7] | 蒋政 .大面积化学气相沉积金刚石自支撑膜的力学性能研究[D].北京科技大学,2000. |
| [8] | Sanchez G O;Gomez A C;Sanchez O J et al.Dielectric and Raman Spectroscopy of MWCVD Diamond Thin Films[J].Journal of Materials Science:Materials in Electronics,1996,7(04):297-303. |
| [9] | Ager J W;Drory M D .Quantitative Measurement of Residual Biaxial Stress by Raman Spectroscopy in Diamond Grown on a Ti Alloy by Chemical Vapor Deposition[J].Physical Review B,1993,48:2601-2607. |
| [10] | Zhang H D;Tian J Z;Tang W Z et al.Correlation between Fracture Strength and Crystal Orientation of Freestanding Diamond Films[J].CARBON,2003,41:579-625. |
| [11] | 郭世斌 .微量杂质对金刚石膜物理性能的影响研究[D].北京科技大学,2009. |
| [12] | 李惠琪;李惠东;何鸣鸿.等离子体喷射法气体生长金刚石[M].北京:煤炭工业出版社,1995:9-10,31-50. |
| [13] | 吕反修,黄天斌,唐伟忠,宋建华,佟玉梅.直流电弧等离子体喷射金刚石厚膜生长不稳定性问题[J].材料热处理学报,2001(01):46-50. |
| [14] | 黄天斌 .DC ARC PLASMA JET大面积金刚石膜沉积的计算机模拟[D].北京:北京科技大学,2001. |
| [15] | 牛得草 .CVD金刚石膜杂质和缺陷的研究[D].北京:北京科技大学,2007. |
| [16] | Goodwin D G .Scalling Laws for Diamond Chemical Vapor Deposition:I Diamond Surface Chemistry[J].Journal of Applied Physics,1993,74:6890-6895. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%