目的：提高45#钢零件的表面硬度和润滑减摩性能。方法在45#钢试样表面进行激光淬火,研究激光功率和扫描速度对淬火表面淬硬层深度和宽度的影响,分析淬硬层不同区域的显微硬度和微观组织。利用二极管泵浦 Nd：YAG 激光加工机在45#钢光滑试样表面加工出具有一定分布规律的微凹坑织构,采用热压法向其中填入由 MoS2、聚酰亚胺和石墨组成的复合固体润滑剂,并与未处理的光滑试样进行摩擦学性能对比。结果将激光织构与淬火技术有效融合,可以使45#钢表面硬度提高至835HV,摩擦系数减小约50%。结论激光织构淬火减摩抗磨复合处理技术能够提高45#钢零件的表面硬度,减小摩擦系数,具有很好的工程应用前景。
Objective To improve the hardness and antifriction properties on 45# steel surface. Methods Laser quenching was performed on the 45# steel surface. The effects on the hardened depth and width of the quenched surface by laser powers and scan-ning speeds were studied. The micro-hardness and micro-structure were analyzed on the different parts of the hardened layer. Uni-form-distributive micro-dimples were conducted on the smooth surface of 45# steel specimens by diode-pumped Nd:YAG laser ma-chine and MoS2-PI-Gr composite solid lubricants were filled into the texture by hot-pressing method, then tribological performance comparison with the untreated smooth 45# steel surface was carried out. Results The hardness of 45# steel surface could reach up to 835HV and the friction coefficient caould be reduced by almost 50% through laser-texturing and quenching composite technology. Conclusion The hardness of 45# steel surface could be increased and the friction coefficient could be reduced by laser-texturing and quenching composite technology, which would have a good engineering application prospect.
参考文献
| [1] | PINKERTON A J,LIN L I . The Effect of Laser Pulse Width on Multiple Layer 316L Steel Clad Microstructure and Sur-face Finish[J].Applied Surface Science,2003,209(2):411-416.,2003. |
| [2] | 李旭东,张连峰,朱武峰,丁文勇.铝合金高温低周疲劳裂纹扩展可靠性评估[J].装备环境工程,2013(05):134-138. |
| [3] | 徐中,王健,李颖.仿生涂层磨损及其与表面形貌的关联性研究[J].表面技术,2013(04):9-11,114. |
| [4] | 韩晓明,高飞,宋宝韫,符蓉.摩擦速度对铜基摩擦材料摩擦磨损性能影响[J].摩擦学学报,2009(01):89-96. |
| [5] | DROZDOV Y N. The Main Problems of the Space Tribology [C]//2nd World Tribology Conference, Austria:Vienna, 2001:382-385.,2001. |
| [6] | 张津,李军,李春天,桑雪梅.金属摩擦表面耐磨自修复技术的研究[J].表面技术,2004(05):7-8. |
| [7] | MAHMOUDI B,TORKAMANY M J,AGHDAM A R,et al . Laser Surface Hardening of AISI 420 Stainless Steel Treated by Pulsed Nd:YAG Laser[J].Materials & Design,2010,31(5):2553-2560.,2010. |
| [8] | 李刚,相珺,况军,贾孟东.GCr15钢表面激光淬火的组织与性能[J].材料热处理学报,2010(04):129-132. |
| [9] | 花银群,陈瑞芳,杨继昌,张永康,李长生,路淼.激光淬火和冲击复合强化处理40Cr钢的耐磨性能研究[J].摩擦学学报,2003(05):448-450. |
| [10] | WANG W J,GUO J,LIU Q Y,et al. Effect of Laser Quenching on Wear and Damage of Heavy-haul Wheel/Rail Materials [J]. Proceedings of the Institution of Mechanical Engineers, Part J:Journal of Engineering Tribology, 2014, 228(1):114-122.,2014. |
| [11] | 李志强,陈昭运.17-4PH不锈钢激光淬火疲劳性能研究[J].热加工工艺,2013(04):196-198,201. |
| [12] | 王文健,刘吉华,郭俊,刘启跃.激光淬火对重载轮轨磨损与损伤性能的影响[J].材料科学与工艺,2012(06):69-72,80. |
| [13] | DA SILVA W M,SUAREZ M P,MACHADO A R,et al . Effect of Laser Surface Modification on the Micro-abrasive Wear Resistance of Coated Cemented Carbide Tools[J].Wear,2013,302(1):1230-1240.,2013. |
| [14] | 符永宏,杨巍,张华伟,华希俊.激光微造型凸轮副的摩擦磨损[J].农业机械学报,2010(01):216-220. |
| [15] | MARQUART M, WAHL M, EMRICH S, et al . Enhancing the Lifetime of MoS2-lubricated Ball Bearings[J].Wear,2013,303(1):169-177.,2013. |
| [16] | 张培耘,华希俊,符永宏,尹必峰.激光表面微织构工艺试验及应用研究[J].表面技术,2013(05):55-58,73. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%