以薄膜厚度和耐点滴腐蚀时间作为衡量Ce-Mn转化膜性能的指标,采用正交实验研究了室温下pH值为2.0时铝合金表面Ce-Mn转化处理液配方及成膜时间对转化膜性能的影响.分别获得两种较佳工艺,配方和成膜时间分别为:10 g/LCe(NO_3)_3+2 g/L KMnO_4+0.06 g/L NaF,12 min;7 g/L Ce(NO_3)_3+1 g/L KMnO_4+0.06 g/L NaF,9 min.采用点滴腐蚀法、极化曲线和交流阻抗研究铝合金表面Ce-Mn转化膜的耐腐蚀性能;采用硬度计、SEM和EDS研究转化膜的表面硬度.形貌及组成,结果表明处理液中添加成膜促进荆NaF后,使转化膜的成膜速率和耐腐蚀性能(耐点滴腐蚀时间)提高,制备Ce-Mn转化膜后,铝合金表面的显微硬度从纯Al时的HV72最人增大至HV532.

NaF was used as the accelerant to accelerate the conversion coating formation on 6063 Al alloy in Ce(NO_3)_3 and KMnO_4 solution. Orthogonal experiments were conducted to find out the optimal process for prepare Ce-Mn conversion coating on Al alloy surface. Coating thickness and anti-corrosion time were taken as the indexes of performance assessment. Two better solution components and coating formation times at room temperature and pH=2.0 were selected to be 10 g/L Ce(NO_3)_3+2 g/L KMnO_4+0.06 g/L NaF, 12 min and 7 g/L Ce(NO_3)_3+1 g/L KMnO_4+0.06 g/L NaF, 9 min. The anti-corrosion ability of coating was evaluated by dropping test, polarization curve and electrochemical impedance spectroscopy. The increase of AE (the different between pinhole corrosion and corrosion potentials) and the decrease of corrosion demonstrate that the anti-corrosion ability of 6063 Al alloy with Ce-Mn conversion coating is greatly enhanced since the cathodic current (i_c) and anodic corrosion current (i_a) decrease. Ce-Mn conversion coating serves as an effective barrier to prevent corrosion attack. Generally, lower C (Capacitance) points out relatively higher degree of surface homogeneity which yields an almost closed capacitive arc. The addition of NaF make C become less, conversion coating resistance (R_c) and charge transfer resistance (R_(ct)) become higher. A thicker and denser coating was formed on the surface of Al alloy, which presents a barrier to O_2 or CO_2 or Cl~- permeation, bring better protection to Al 6063 alloy. The surface hardness was determined by micro-hardness test, the micro-morphology, and compositions of coatings were analysed by SEM and EDS. With NaF added, the surface hardness becomes stronger. Formation time was also an important factor to prepare a high-quality coating, corrosion resistance of Ce-Mn conversion coating was more effective when formation time is 9 min than when it is 15 min. The results of orthogonal experiments show that the optimal coating processing is 7 g/L Ce(NO_3)_3+ 1 g/L KMnO_4+0.06 g/L NaF, 9 min. The addition of NaF can accelerate the coating formation, increase the Ce and Mn content in coating and thus improve the coating anti-corrosion performance. It is found that the surface micro-hardness increases from HV72 of pure Al surface to HV532 of Al alloy surface with Ce-Mn conversion coating.

参考文献

[1] Zhang J T,Yang C Y,Pan L,Li C D.Acta Metall Sin,2008; 44:1372(张金涛,杨春勇,潘亮,李春东.金属学报,2008;44:1372)
[2] Wang H,Wang H W.Trans Nonferrous Met Soc Chin,2004; 14 (suppl.1):166
[3] Chen N C,Ao H M,Zhan Z L.Mater Sci Forum,2009; 610-613:29
[4] Pohlein M,Bertran R U,Wolf M,Eldik R V.Anal Bioanal Chem,2009; 394:583
[5] Zhang S L,Zhang X L.Corns Sci Prot Technol,2008; 20:279(张圣麟,张小麟.腐蚀科学与防护技术,2008;20:279)
[6] Hamdy A S.Mater Lett,2006; 60:2633
[7] Yu H C,Chen B Z,Shi X C,Wu H Y,Li B.J Appl Elec-trochem,2009; 39:303
[8] Mishra A K,Balasubramaniam R.Corros Sci,2007; 49:1027
[9] Dabala M,Ramous E,Magrini M.Mater Corros,2004; 55:381
[10] Hu J M,Liu L,Zhang J Q,Cao C N.Chem J Chin Univ,2006; 27:1125(胡吉明,刘谅,张鉴清,曹楚南.高等学校化学学报,2006;27:1125)
[11] Hinton B R W,Arnott D R,Ryan N E.Appl Surf Sci,1985; 22-23(5):236
[12] Hasannejad H,Shahrabi T,Aliofkhazraei M.Rare Met,2009; 28:98
[13] Chen D C,Li W F,Gong W H,Wu G X,Huang M S,Liang Y Q.Chin J Nonferrous Met,2008; 18:1939(陈东初,李文芳,龚伟惠,吴桂香,黄铭深,梁奕清.中国有色金属学报,2008;18:1939)
[14] Yu X W,Zhou D R,Yin Z D,Zhou Y H.Chin J Nonferrous Met,1999; 9:73(于兴文,周德瑞,尹钟大,周育红.中国有色金属学报,1999;9:731
[15] Decroly A,Petitjean J P.Surf Coat Technol,2005; 194:1
[16] Tjong S C,Huo H W.J Mater Eng Perform,2009; 18:88
[17] Yu X W,Cao C N,Yan C W,Lin H C,Zhou D R,Yin Z D.Acta Metall Sin,2000; 36:979(于兴文,曹楚南,严川伟,林海潮,周德瑞,尹钟大.金属学报,2000;36:979)
[18] Chen S,Chen X F,Liu C Y,Zhu L,Sun J Q.Mater Prot,2003; 36(8):33(陈溯,陈晓帆,刘传烨,朱莉,孙际琪.材料保护,2003;36(8):33)
[19] Myers D,translated by Wu D C,Zhu P X,Wang L X,Gao X S.Surface,Interface,and Colloids:Principles and Applications.2nd ed.,Beijing:Chemical Industry Press,2005:136(Myers D著,吴大诚,朱谱新,王罗新,高绪珊译.表面、界面和胶体-原理及应用.第二版,北京:化学工业出版社,2005:136)
[20] Zhang K C,Zhang L H.Crystal Growth.Beijing:Science Press,1981:163(张克从,张乐潓.晶体牛长.北京:科学出版社,1981:163)
[21] Hinton B R W.J Alloys Comp,1992; 180:15
[22] Palomino L E M,Suegama P H,Aoki I V,Paszti Z,Melo H G D.Electrochim Acta,2007; 52:7496
[23] Liu S,Xu N N,Duan J M,Zeng Z O,Feng Z P,Xiao R.Corros Sci,2009; 51:1356
[24] Kosec T,Merl D K,Milosev I.Corros Sci,2008; 50:1987
[25] Song F M,Jones D A,Kirk D W.Corrosion,2005; 61:145
[26] Hazzazi O A.J Appl Electrochem,2007; 37:933
[27] Hasenay D,Seruga M.J Appl Electrochem,2007; 37:1001
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%