以廉价易得的氯化钡、四氯化钛为原料,在240℃下仅用12h水热合成得到四方相钛酸钡纳米粉末,从而为该纳米粉末的产业化提供了简便条件.水热产物经XRD、SEM、XRF等手段表征,发现提高氢氧化钠过量的浓度、降低反应物四氯化钛浓度有利于四方相钛酸钡纳米粉末的生成,同时在水热产物中没有发现碳酸根和氯离子等残余的杂质,表明产物具有较高的纯度.产物粒度小于100nm,比表面积为12m2/g.
参考文献
| [1] | 施而畏 等.[J].无机材料学报,1995,10(04):385-390. |
| [2] | Reza Asiaie;Weidong Zhu;Sheikh A. Akbar;Prabir K. Dutta .Characterization of Submicron Particles of Tetragonal BaTiO_3[J].Chemistry of Materials,1996(1):226-234. |
| [3] | James OE;Jr et al.[J].Journal of the American Ceramic Society,1996,79(11):2929-2939. |
| [4] | Malgorzata M Lencka et al.[J].Chemistry of Materials,1993,5:61-70. |
| [5] | Araujo F.G.S.;Filho A.A.M. .THE INFLUENCE OF THE PROCESSING CONDITIONS ON THE PROPERTIES OF HYDROTHERMAL PROCESSED BARIUM TITANIUM OXIDE POWDERS[J].Scripta materialia,2000(5):447-452. |
| [6] | DuttaPK et al.[J].Chemistry of Materials,1994,6(09):542-548. |
| [7] | Wu MM et al.[J].Journal of the American Ceramic Society,1999,82(11):3254-3256. |
| [8] | Urek S et al.[J].Journal of the European Ceramic Society,1998,18:279-286. |
| [9] | 夏长泰 等.[J].无机材料学报,1995,10(03):293-299. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%