对重钢炼钢厂因钢水可浇性原因导致的连铸机非计划断浇事故进行分析，认为主要原因是堵塞，包括钢水温度低水V1堵塞，钢包水口堵塞、中间包水口堵塞和中间包上水口碗部堵塞；其次是塞棒的异常侵蚀影响塞棒的控流。通过采取预防措施，铸机非计划断浇次数由1．8次／月降低至0．8次／月，钢种改判炉次由1．4炉／月降低至0．6炉／月，生产实践效果较好。
The reasons for the continuous casting machine casting off of non-program caused by pouring of molten steel was analyzed. The main reason is considered to be blocked, which covers the low-temperature molten steel outlet plug, plug nozzle ladle, tundish and tundish nozzle blockage, and the department of plug nozzle bowl followed by abnormal erosion Stopper Stopper impact of control flow. Taking preventive measures, the number of casting machine casting off of non-plan decreased from 1.8 times/month to 0.8 times/month, steel furnace revision from the 1.4 oven/stove to the 0.6/month, and the production practice is better.
参考文献
| [1] | 陈雷.连铸铸钢[M].北京:冶金工业出版社,1994 |
| [2] | 邱明金.钢包用高铝质水口发生堵塞的原因及对策[J].国外耐火材料,2001(04):15-21. |
| [3] | 彭平;裴云毅;许春雷 等.300吨钢包水口结瘤分析[J].钢铁,1990,25(11):15. |
| [4] | 魏春新,王志英,张崇民.铝改硅镇静钢浇注钢包水口堵塞原因及预防措施[J].连铸,2001(03):36-38. |
| [5] | 王庆祥,吴雄,喻承欢,陈清泉,李具中,吴永生.浸人式水口堵塞的机理及其改善措施[J].钢铁,2005(02):34-36. |
| [6] | 吴伟,吴巍,刘跃,刘浏.方坯连铸机浸入式水口堵塞机理的探讨[C].2007年中国钢铁年会,2007 |
| [7] | 谢集祥,尹振芝,王庆祥.连铸中间包水口堵塞问题浅析[J].中国冶金,2006(03):8-9,20. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%