目的：考查苯胺三聚体( AT)添加量对涂层防腐蚀性能的影响。方法自制苯胺三聚体，以苯胺三聚体和异佛尔酮二胺( IPD)为共固化剂，制备环氧涂层。对苯胺三聚体的化学结构进行表征，对涂层的表面微观形貌进行观察，通过电化学手段及盐雾实验评价涂层的防腐蚀效果。结果苯胺三聚体的加入使得环氧树脂涂层的防腐蚀性能有明显提升，并且苯胺三聚体的含量越高，涂层防腐蚀效果越好。对于不加传统固化剂的涂层，由于固化效果不佳，会导致防腐性能骤减。结论使用AT与IPD共固化环氧树脂涂层，当固化剂中AT的摩尔分数为80%时，涂层具有最佳的性能。
Objective To study the influence of the amount of aniline trimer on the corrosion resistance of the coating. Methods Epoxy coating was cured by aniline trimer ( AT) and isophorone dianime ( IPD) . The chemical structure of aniline trimer was char-acterized by IR and NMR. The surface morphology of coating was observed by SEM. The anticorrosion ability of the coating was e-valuated by electrochemical method and salt spray test. Results The anticorrosion ability of the coating was improved by the addi-tion of AT, and the anticorrosion ability increased with the increasing AT content. However, curing by solely AT destroyed the structure of the coating which reduced the anticorrosion effect. Conclusion The results demonstrated that the best anticorrosion a-bility was obtained when the weight ratio of AT/IPD was 4 : 1.
参考文献
| [1] | 王荣华,李晖,孙岩,刘亚平.橡胶材料加速老化研究现状及发展趋势[J].装备环境工程,2013(04):66-70,101. |
| [2] | 张勇,丁文勇,陈跃良,张泰峰.有机涂层户外曝晒与加速试验对比研究[J].装备环境工程,2013(02):14-17,70. |
| [3] | 奚愚生,杨晓东,刘光明.溶胶-凝胶法制备杂化材料的研究进展[J].表面技术,2012(03):120-123. |
| [4] | A.M. Youssef;S. Kamel;M. El-Sakhawy .Structural and electrical properties of paper-polyaniline composite[J].Carbohydrate Polymers: Scientific and Technological Aspects of Industrially Important Polysaccharides,2012(2):1003-1007. |
| [5] | 张静,冯玉坤,万小梅,吕平.导电聚苯胺的制备及其在防腐涂料中的应用[J].现代涂料与涂装,2011(03):12-14,26. |
| [6] | Baldissera, A.F.;Ferreira, C.A. .Coatings based on electronic conducting polymers for corrosion protection of metals[J].Progress in Organic Coatings: An International Review Journal,2012(3):241-247. |
| [7] | Xin-Gui Li;Mei-Rong Huang;Pan Pan .Synthesis and characterization of a soluble terpolymer from pyridylamine, aniline and xylidine[J].Polymer Degradation and Stability,2001(3):333-341. |
| [8] | 张春,张红明,李应平,李季,王献红.聚苯胺水性涂料的制备及其防腐性能[J].应用化学,2012(05):504-509. |
| [9] | 郝春静,湛含辉,王晓.硅烷偶联剂链长对纳米TiO2表面改性的影响[J].表面技术,2013(02):10-13. |
| [10] | Tahmasebi, E.;Yamini, Y.;Mehdinia, A.;Rouhi, F. .Polyaniline-coated Fe _3O _4 nanoparticles: An anion exchange magnetic sorbent for solid-phase extraction[J].Journal of separation science,2012(17):2256-2265. |
| [11] | Pramanik, S.;Karak, N.;Banerjee, S.;Kumar, A. .Effects of solvent interactions on the structure and properties of prepared PAni nanofibers[J].Journal of Applied Polymer Science,2012(3):830-836. |
| [12] | DONG J Q;SHEN Q .Comparison of Polyaniline Doped by Lignosulfonates with Three Different Ions[J].Journal of Applied Polymer Science,2012,126:E10-E16. |
| [13] | 封伟,韦玮,吴洪才.可溶导电聚苯胺的合成及其性能研究[J].功能高分子学报,1998(02):237-240. |
| [14] | Chang-Jian Weng;Chi-Hao Chang;Chih-Wei Peng .Advanced Anticorrosive Coatings Prepared from the Mimicked Xanthosoma Sagittifolium-leaf-like Electroactive Epoxy with Synergistic Effects of Superhydrophobicity and Redox Catalytic Capability[J].Chemistry of Materials: A Publication of the American Chemistry Society,2011(8):2075-2083. |
| [15] | 景遐斌,王利祥,王献红,耿延候,王佛松.导电聚苯胺的合成、结构、性能和应用[J].高分子学报,2005(05):655-663. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%