The orientation dependence of creep rupture lives of a single crystal superalloy at 760 oC/760 MPa was investigated. The orientations of the specimens tested were about 30o away from [001]. The results showed that specimens with orientations on the [001]-[011] boundary had the longest rupture life. The deformation of these specimen were controlled by a/2<110> slip and a few stacking faults with two orientations were observed. On the other hand, specimens with orientations near the [001]-[011] boundary or on the [001]- [¹111] boundary showed short rupture lives, and stacking faults with single orientation were observed in these specimens. The rupture properties and the deformation mechanisms were discussed based on the dislocation pattern and the calculated Schmid factors for different specimens..
参考文献
| [1] | W. Betteridge and S.W.K. Shaw: Mater. Sci. Technol., 1987, 3, 682.[2 ] D.N. Duhl: in Superalloys II, ed. C.T. Sims, N.S. Stoloff and W.C. Hagel, John Wiley and Sons, New York, 1987.[3 ] F.R.N. Nabarro and H.L.d. Villiers: in The Physics of Creep, London, 1995.[4 ] G.R. Leverant and B.H. Kear: Metall. Trans., 1970, 1, 491.[5 ] B.H. Kear and B.J. Piearcey: Trans. TMS-AIME, 1967, 239, 1209.[6 ] R.A. Mackay and R.D. Maier: Metall. Trans. A, 1982, 13, 1747.[7 ] C.M.F. Rae, N. Matan, D.C. Cox, M.A. Rist and R.C. Reed: Metall. Mater. Trans. A, 2000, 31, 2219.[8 ] J.L. Liu, T. Jin, J.H. Zhang and Z.Q. Hu: Acta Metall. Sin., 2001, 37, 1233. (in Chinese)[9 ] J.L. Liu, T. Jin, X.F. Sun, J.H. Zhang, H.R. Guan and Z.Q. Hu: Mater. Sci. Eng. A, 2007, 479, 277.[10] Y.X. Jia, T. Jin, J.L. Liu, X.F. Sun and Z.Q. Hu: Acta Metall. Sin., 2009, 45, 1364. (in Chinese)[11] L. Shui, T. Jin and Z.Q. Hu: Acta Metall. Sin., 2009, 45, 1349. (in Chinese)[12] S.S.K. Gunturi, D.W. MacLachlan and D.M. Knowles: Mater. Sci. Eng. A, 2000, 289, 289.[13] J. Zhang and L.H. Lou: J. Mater. Sci. Technol., 2007, 23, 289.[14] V. Sass, U. Glatzel and M. Feller-Kniepmeier: Acta Mater., 1996, 44, 1967.[15] C.M.F. Rae and R.C. Reed: Acta Mater., 2007, 55, 067.[16] G.L. Drew, R.C. Reed, K. Kakehi and C.M.F. Rae: in Superalloys 2004, eds K.A. Green, T.M. Pollock, H. Harada, T.E. Howson, R.C. Reed, J.J. Schirra and S. Walston, TMS, New York, 127.[17] M. Feller-Kniepmeier and T. Kuttner: Acta Metall. Mater., 1994, 42, 3167.[18] T.M. Pollock and R.D. Field: in Dislocations in Solids, Elsevier, Amsterdam, 2002, 567.[19] M. Condat and B. Decamps: Script. Metall., 1987, 21, 607.[20] J. Courbon, F. Louchet, M. Ignat, J. Pelissier and P. Debrenne: Phil. Mag. Lett., 1991, 63, 73.[21] P. Caron, T. Kahn and P. Veyssiere: Philos. Mag. A, 1988, 57, 859.[22] N. Matan and D.C. Cox: Acta Mater., 1999, 47, 1549. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%