Preparation and Arc Breakdown Behavior of Nanocrystalline W-Cu Electrical Contact Materials

材料科学技术（英文）, 2005, 21(6): 875-878.

^1, , ^2, , ^3,

1.School of Materials Science and Engineering, Xi'an University of Technology, Xi'an 710048, China;Department of Materials Physics, Xi'an Jiaotong University, Xi'an 710049, China

2.Department of Materials Physics, Xi'an Jiaotong University, Xi'an 710049, China

3.Department of Materials Physics, Xi'an Jiaotong University, Xi'an 710049, China

基金项目: 中国科学院资助项目(50071043) the Nat-ural Science Fundation of Shaanxi province under(2004E105)

Preparation and Arc Breakdown Behavior of Nanocrystalline W-Cu Electrical Contact Materials

Keywords： Nanostructured materials

Nanostructured (NS) W-Cu composite powder was prepared by mechanical alloying (MA), and nanostructured bulk of W-Cu contact material was fabricated by hot pressed sintering in an electrical vacuum furnace. The microstructure,electric conductivity, hardness, breakdown voltage and arcing time of NS W-Cu alloys were measured and compared to conventional W-Cu alloys prepared by powder metallurgy. The results show that microstructural refinement and uniformity can improve the breakdown behavior, the electric arc stability and the arc extinction ability of nanostructured W-Cu contacts materials. Also, the nanostructured W-Cu contact material shows the characteristic of spreading electric arcs, which is of benefit to electric arc erosion.

参考文献

[1]	L J Kecskes;M D Trexler;B R Klotz;K C Choand,R J Dowding .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2001,32(11):2885.
[2]	B Thomas;K V Walter;M Rol;K E Sacegr .[J].IEEE Transactions,1991,14(01):8.
[3]	C S Xiong;Y H Xiong;H Zhu;T F Sun,J H Yu .[J].Nano-Structured Materials,1995,5(05):425.
[4]	J C Kim;S S Ryu;Y D Kim;I H Moon .[J].Scripta Materialia,1998,39(06):669.
[5]	J C Kim;S S Ryu;I H Moon .[J].Journal of Advanced Materials,1999,31(04):37.
[6]	D. Y. Ying;D. L. Zhang .Effect of high energy ball milling on solid state reactions in Al-25 at. - percent Ni powders[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2001(7):815-822.
[7]	J C Kim;I H Moon .[J].Nano-Structured Materials,1998,10(02):283.
[8]	J Kaczmar .[J].Powder Metallurgy,1989,32(03):171.
[9]	B J Ding;Z Yang;X Wang .[J].IEEE Transactions on Components Packaging and Manufacturing Technology,1996,19(01):76.
[10]	陈文革,丁秉钧,张晖.机械合金化制备的纳米晶W-Cu电触头材料[J].中国有色金属学报,2002(06):1224-1228.
[11]	H Zhang;Z Yang;B Ding .[J].IEEE Transactions on CPT Part A,1999,22(03):455.
[12]	Y Wang;B J Ding .[J].IEEE Transactions on CPT Part A,1999,22(03):467.
[13]	F Wang;F Zhuge;H Zhang;B Ding .[J].Materials Research Bulletin,2003,38:629.
[14]	Y Wang;C Zhang;H Zhang;B Ding,K Lu .[J].Journal of Physics D:Applied Physics,2003,364:2649.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Preparation and Arc Breakdown Behavior of Nanocrystalline W-Cu Electrical Contact Materials

参考文献