采用稀土草酸盐先驱体法制各了LaPO4:Ce,Tb绿色荧光粉.借助X射线衍射(XRD)、扫描电镜(SEM)、比表面仪及荧光分光光度计研究了荧光粉的制备过程,并对其晶体结构、表观形貌、粒径、比表面积、孔径分布、发光特性等进行分析和表征.结果表明:先驱体在900℃还原气氛下煅烧,制备的产物属于正磷酸盐的单斜晶系,独居石结构.颗粒形状接近球形,粒径分布在lOo～150nm.比表面积为7.3 m2/g,孔径分布较宽.同时,在286 nm紫外光激发下发绿光,发射主峰位于543 nm,对应于Tb3+的5D4→7F5跃迁发射.
参考文献
| [1] | Fang Wang;Hongwei Song;Guohui Pan et al.[J].发光杂志,2008,128(12):2013. |
| [2] | Zhenxiao Fu;Wenbo Bu .High efficiency green-luminescent LaPO_4:Ce,Tb hierarchical nanostractures: Synthesis, characterization, and luminescence properties[J].Solid state sciences,2008(8):1062-1067. |
| [3] | 杨定明,朱达川,戴亚堂,庄稼,涂铭旌.室温固相反应前驱体法合成稀土磷酸盐绿色荧光粉[J].稀有金属材料与工程,2005(03):436-438. |
| [4] | Wuled Lenggoro I;Bin Xia;Hiroaki Mizushima et al.[J].Materials Letters,2001,50:92. |
| [5] | Yun Chan Kang;Eun Joung Kim;Dong Youl Lee .High brightness LaPO_4:Ce,Tb phosphor particles with spherical shape[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):266-270. |
| [6] | Junker;Grosseau P et al.[J].Powder Technology,2005,154(2-3):132. |
| [7] | 袁剑辉,王修琼,张振华.（La,Ce,Tb）PO4的合成及应用特性研究[J].稀有金属,2005(06):875-879. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%