Three cement samples were prepared, including OPC consisted of 100wt% portland cement, PFA consisted of 70wt% portland cement and 30wt% fly-ash, and CA consisted of 70wt% portland cement and 30wt% modified fly ash. The strength of hardened cement paste of these samples was tested and their pore structures were determined by a mercury intrusion porosimeter. Moreover,the data of the pore structures of three samples were comprehensively analyzed. The relations between the pore structures and the compressive strength of the three samples were studied. The experimental results show that the relations between the porosity determined by the mercury intrusion porosimeter and the compressive strength are not notable, and the total pore surface area, the average pore diameter and the median pore diameter could be used to explain the difference of the strength of the tested samples.
参考文献
| [1] | Taylor H F W.Cement Chemistry(2 edition)[M].London:Thomas Telford Press,1997 |
| [2] | Hewlett P C.Les's Chemistry of Cement and Concrete(4 edition)[M].London:Arnold,1998 |
| [3] | Wu Zhongwei;Lian Huizhen.High Performance Concrete[M].北京:中国铁道出版社,1999 |
| [4] | Mehta P K;Manmohan D.Pore Size Distribution and Permeability of Hardened Cements Pastes[A].France Paris,1980:1-5. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%