研究了共聚型马酸酐系减水剂的制备与性能.以马来酸酐和聚乙二醇(PEG)为原料,经酯化制得酯化物单体;并测定其酯化率,用 IR 表征了酯化物的结构.以马来酸聚乙二醇单酯、2-丙烯酰胺-2-甲基丙磺酸(AMPS)和甲基丙烯酸为原料通过共聚反应制得减水剂,讨论了共聚反应中影响减水剂净浆流动度的因素,并用GPC表征了共聚物减水剂的分子量及分布.将减水剂添加到水泥浆中制得水泥石样品,通过SEM分析了水泥的早期微观结构.结果表明,当 n(酯化物):n(MAA);n(AMPS)=1:3:1.5时所得减水剂净浆流动度为265mm,GPC分析表明减水剂平均分子量Mn=12562,分散系数Mw/Mn=2.1361,SEM分析表明减水剂使水泥石大孔减少,生成了更多较小的孔,结晶生长更密实.
参考文献
| [1] | I. PAPAYIANNI;G. TSOHOS;N. OIKONOMOU .Influence of superplasticizer type and mix design parameters on the performance of them in concrete mixtures[J].Cement & concrete composites,2005(2):217-222. |
| [2] | Kreppelta F;Weibelb M;Zampinib D et al.Influence of solution chemistry on the hyaration of polished clinker surfaces--A study of different types of polycarboxylic acid-based admixtures[J].Cement and Concrete Research,2002,32(01):187. |
| [3] | K. Yamada;T. Takahashi .Effects of the chemical structure on the properties of polycarboxylate- type superplasticizer[J].Cement and Concrete Research,2000(2):197-207. |
| [4] | Uchikawa H;Sawaki D;Hanehara S .Influence of kind and added timing of organic a-dmixture on the composition,structure and propertyoffresh cement paste[J].Cement and Concrete Research,1999,25(02):353. |
| [5] | 李祟智,李永德,冯乃谦.聚羧酸系减水剂结构与性能关系的试验研究[J].混凝土,2002(04):3-5,14. |
| [6] | 王立宁,张福强,李伟光,任丽,王立新.聚羧酸减水剂的合成及分散性能研究[J].混凝土,2006(01):104-106. |
| [7] | Tanaka Y;Ohta A;Hirata T et al.Cement composition using the dispersant of (meth)acrylic-esters,(metha)acrylic acids polymers[P].US,6187841,2001-02-13. |
| [8] | Hirata T;Tanaka H;Yuasa T .Method for production of esterified product and apparatus t-herefore[P].US,6362364,2002-03-26. |
| [9] | 马保国,张慢,谭洪波,李亮.聚羧酸减水剂侧链密度对水泥早期水化特性的影响[J].新型建筑材料,2008(06):41-44. |
| [10] | 赵石林,岳阳,黄小彬.聚羧酸盐多元共聚物高效减水剂的研制[J].化学建材,2000(04):37-39. |
| [11] | 李崇智 .新型聚羧酸系减水剂的合成及其性能研究[D].清华大学,2004. |
| [12] | GB/T 8077-2000.GB/T 8077-2000.混凝土外加剂匀质性试验方法[S].,2000. |
| [13] | 刘其城;徐协文;陈曙光.混凝土外加剂[M].北京:化学工业出版社,2008:72. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%