为了获得高锌超高强铝合金均匀化退火适宜工艺,采用光学显微镜、差示扫描量热法、扫描电镜、能谱分析等方法研究二极均匀化退火工艺对高锌Al-Zn-Mg-Cu合金的组织和T6(120 ℃×24 h)人工时效后的力学性能的影响.结果表明,合金经400℃,4h均匀化后的过烧温度为471℃;实验合金的最佳二级均匀化退火工艺为随炉升温到400℃保温4h,再随炉升温到467℃保温30 h;合金经该均匀化工艺处理后,铸锭中的元素偏析明显消除,共晶相明显减少,合金挤压态析出相较小且分布均匀,合金力学性能明显改善.
参考文献
[1] | Engdahl T;Hansen V;Warren P J et al.Investigation of fine precipitates in Al-Zn-Mg alloys after various heat treatments[J].Rare Metal Materials and Engineering,2002,327(01):59-64. |
[2] | L. K. BERG;J. GJONNES;V. HANSEN .GP-ZONES IN Al-Zn-Mg ALLOYS AND THEIR ROLE IN ARTIFICIAL AGING[J].Acta materialia,2001(17):3443-3451. |
[3] | Keams M A .The mechanism of phase transformations in crystalline solids[J].Light Metals,1996,59(17):713-720. |
[4] | 刘晓涛,董杰,崔建忠,赵刚.高强铝合金均匀化热处理[J].中国有色金属学报,2003(04):909-913. |
[5] | 张万金;王美琪 .LD11铸锭均匀化试验及过烧温度的确定[J].轻合金加工技术,1998,26(07):40-43. |
[6] | 段玉波,唐剑,曾苏民.阶段均匀化处理对7A04合金均匀化程度和过烧温度的影响[J].铝加工,2003(03):23-26,58. |
[7] | 龚澎,张坤,戴圣龙.一种新型Al-Zn-Mg-Cu系铝合金的均匀化工艺研究[J].航空材料学报,2009(05):33-38. |
[8] | Park J K;Ardell A J .Effect of retrogression and reaging treatments on the microstructure of Al-7075-T7651[J].metallurgical and materials transactions a-physical metallurgy and materials science,1984,15(08):1531-1543. |
[9] | Delasi R;Adler P N .Calorimetric studies of 7000 series aluminum alloys:Ⅰ.Matrix precipitate characterization of 7075[J].metallurgical and materials transactions a-physical metallurgy and materials science,1977,8(07):1177-1183. |
[10] | Hornbogen E .Formation of nm-size dispersion from supersaturated solid solutions of aluminum[J].materials science forum,2000,331(337):879-888. |
[11] | Nie J F;Muddle B C;Polmear I J .The effect of precipitate shape and orientation on dispersion strengthening in high strength aluminum alloys[J].materials science forum,1996,217(222):1257. |
[12] | Waterloo G;Hansen V;Gjonnes J et al.Effect of predeformation and preaging at room temperature in Al-Zn-Mg-(Cu,Zr) alloys[J].Rare Metal Materials and Engineering,2001,303(1-2):226-233. |
[13] | Gale W F;Totemeir T C.Smithhells Metal Reference Book[M].Butterworth-Heinemann Ltd,2004:1. |
[14] | Mats Hillcrt;赖和怡;刘国勋.合金扩散和热力学[M].北京:冶金工业出版社,1984:52. |
[15] | 宁爱林,刘志义,冯春,曾苏民.Al-Zn-Mg-Cu合金组织和电导率及抗应力腐蚀性能研究[J].材料热处理学报,2008(02):108-113. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%