由于树脂基复合材料层合板对冲击作用比较敏感,因此,在使用过程中受到低能冲击时,极易产生不可见损伤,造成复合材料在强度和刚度上的损失,严重威胁结构的安全使用性.本文借助四点弯曲实验分别对五种不同铺层的乙烯基树脂/玻纤复合材料拐角在不同能量冲击后的弯曲刚废衰减进行了测试,讨论了不同铺层和冲击能量对复合材料拐角抗冲性能的影响.研究结果表明,随着冲击能量的增加,冲击损伤越明显,剩余弯曲刚度越低,各种铺层冲击破坏面积与刚度下降呈现基本一致的趋势;相邻铺层的铖层角相差越小,复合材料拐角的弯曲刚度越大,冲击后弯曲刚度损耗越小,[45°/0°/-45°/90°]铺层的冲击后刚度损失率最低,正交铺层的试样组抗冲击性能最差.
参考文献
| [1] | Sala G .Post-impact behavior of aerospace composites experiments and simulations[J].COMPOSITES PART B-ENGINEERING,1997,28(5-6):651-665. |
| [2] | Lee D G;Cheon S S .Impact Characteristics Glass Fiber Composites with Respect to Fiber Volume Fraction[J].Journal of Composite Materials,2001,35(01):27-54. |
| [3] | M.F.S.F. de Moura;A.T. Marques .Prediction of low velocity impact damage in carbon-epoxy laminates[J].Composites, Part A. Applied science and manufacturing,2002(3):361-368. |
| [4] | Choi H Y;Downs R J;Chang F K .A new approach toward understanding damage mechanisms and mechanics of laminated composite due to low-velocity impact,Part Ⅰ:Experiments[J].Journal of Composite Materials,1991,25(08):992-1011. |
| [5] | Hitchen S A;Ogin S L;Smith P A;Soutis C .The effect of fiber length on fracture toughness and notched strength of short carbon fiber/epoxy composites[J].COMPOSITES,1994,25(06):407-413. |
| [6] | Park R;Jang J .A study of the impact properties of composites consisting of surface-modified glass fibers in vinyl ester resin[J].Composites Science and Technology,1998,58(06):979-985. |
| [7] | 林智育,许希武.含任意椭圆核各向异性板杂交应力有限元[J].固体力学学报,2006(02):181-185. |
| [8] | 张彦中,宁荣昌.复合材料层合板抗冲击损伤的参数表征[J].航空材料学报,1995(01):56. |
| [9] | 沈真,杨胜春,陈普会.复合材料层压板抗冲击行为及表征方法的实验研究[J].复合材料学报,2008(05):125-133. |
| [10] | 沈真;刘俊石 .两种不同韧性复合材料体系抗冲击和损伤性能的试验研究,623S-200201-119[R].中国飞机强度研究所科技档案,2002. |
| [11] | 沈真.含缺陷复合材料层压板的压缩破坏机理[J].航空学报,1991(03):105. |
| [12] | 郑锡涛;沈真 等.低速冲击与准静态压痕力复合材料层合板的损伤等效性[J].航空学报,2010,31(05):928-933. |
| [13] | 庄茁,宋恒旭,彭涛,汪丽媛.复合材料低速冲击损伤研究及等效模型的应用[J].工程力学,2012(z2):15-22. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%