以MgCl_2·6H_2O、CaCO_3和LiCl为原料,采用熔盐法制备了岩层形貌MgO粉体.借助热重-差示扫描热量计(TG-DSC)、X射线衍射仪(XRD)、场发射扫描电子显微镜(SEM)等手段对反应过程及产物进行了分析和表征.结果表明,430 ℃保温3 h热处理,产物中有MgO生成,600 ℃保温3 h热处理,产物经无水乙醇洗涤后,全部为MgO晶体;原料在650 ℃下保温3 h热处理,用水浸泡得到的氢氧化镁为不规整的片状形貌,分解为氧化镁后变成颗粒状形貌,粒径介于0.1～0.6 μm之间;EDTA-PEG溶液浸泡得到的氢氧化镁为四面体形貌,分解为氧化镁后为岩层形貌,大部分在顶角处有缺损,最大边长可达1.5 μm,表层粘附着少量颗粒状氧化镁,表面不平整.
Layered rock configuration MgO powders were prepared through molten salt synthesis with MgCl_2·6H_2O, CaCO_3 ,LiCl as raw materials.They were studied by using XRD and TEM while reactants were investigated by TG-DSC and XRD.The results indicated that MgO was formed at 430 ℃ calcined for 3 h.When calcined at 600 ℃, only MgO product existed in the resultant after washed by Ethanol. If raw materials calcined at 650 ℃ for 3 h,Mg(OH)_2 powders soaked by water were non-regular flakes.They changed into non-regular granular shapes when decomposed to MgO with 0.1-0.6 μm in diameter. On the other side, Mg(OH)_2 powders soaked by PEG-EDTA solution were tetrahedrons.They changed into layered rock configurations with vertex defected when decomposed to MgO,which brim were up to 1.5 μm in length.Linked by some granular,MgO were non-smooth surface.
参考文献
| [1] | Mishra, B;Olson, DL .Molten salt applications in materials processing[J].The journal of physics and chemistry of solids,2005(2/4):396-401. |
| [2] | J.-H. Kim;S.-T. Myung;Y.-K. Sun .Molten salt synthesis of LiNi{sub}0.5Mn{sub}1.5O{sub}4 spinel for 5 V class cathode material of Li-ion secondary battery[J].Electrochimica Acta,2004(2):219-227. |
| [3] | Hsiang H I;Chang C H .Molten salt synthesis and magnetic properties of 3BaO_2@CoO@12Fe_2O_3 powder[J].Journal of Magnetism and Magnetic Materials,2004,278(1-2):218-222. |
| [4] | Shinobu Hashimoto;Shaowei Zhang;William Edward Lee .Synthesis of Magnesium Aluminate Spinel Platelets from alpha-Alumina Platelet and Magnesium Sulfate Precursors[J].Journal of the American Ceramic Society,2003(11):1959-1961. |
| [5] | 《中国药物大词典》编委会.中国药物大词典[M].下册,北京:中国医药科技出版社,1991 |
| [6] | 徐旺生,宣爱国.由白云石制备特种硅钢级氧化镁工艺研究[J].化工矿物与加工,2002(01):4-6. |
| [7] | S.K. Shukla;G.K. Parashar;A.P. Mishra;Puneet Misra;B.C. Yadav;R.K. Shukla;L.M. Bali;G.C. Dubey .Nano-like magnesium oxide films and its significance in optical fiber humidity sensor[J].Sensors and Actuators, B. Chemical,2004(1):5-11. |
| [8] | Lee J H;Jeong T W;Yun S G et al.Thickness effect on secondary electron emission of MgO layer[J].Applied Surface Science,2001,174:62-69. |
| [9] | 李克,聂聪,吕功煊,刘建福.Ni-Sm-MgO催化热解CO制备碳纳米管[J].分子催化,2005(06):419-424. |
| [10] | Guilmeau E.;Andrzejewski B.;Noudem JG. .The effect of MgO addition on the formation and the superconducting properties of the Bi2223 phase[J].Physica, C. Superconductivity and its applications,2003(3/4):382-390. |
| [11] | Cockayne B;Filby J D .The growth of MgO crystal from the vapor[J].Journal of Crystal Growth,1971,9:340-345. |
| [12] | Shintani Ryochi .Magnesia Whisker and its Formation Thereof[P].Japan:JP5 105423,1993. |
| [13] | Thoms H.;Reller A.;Epple M. .THE THERMAL DECOMPOSITION OF MAGNESIUM ALCOHOLATES TO MAGNESIA (MGO) - STUDIES BY IR AND THERMAL ANALYSIS[J].Solid state ionics,1997(1):79-84. |
| [14] | Inchyuan H;Yuhuan X;John D .Electrical and optical properties of MgO thin film prepared by Sol-gel technique[J].Journal of Sol-Gel Science and Technology,1997,9:295-301. |
| [15] | Yin Y D;Zhang G T;Xia Y N .Synthesis and characternation of MgO nanowires through a vapor-phase precursor method[J].Advanced Functional Materials,2002,12(04):293. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%