通过恒温拉伸试验测定了10CrNi5MoV钢在室温至930℃温度范围内的断后延伸率和强度,采用热膨胀法测定了试验钢的特征转变温度Ac1、Ac3.结果表明,10CrNi5MoV钢在730 ～770℃温度区间内断后延伸率超过100％,表现出超塑性行为;热膨胀法测定试验钢的特征转变温度Ac1为680℃,Ac3为784℃.钢板具有超塑性行为的温度位于两相区.
参考文献
| [1] | 胡正寰;夏巨湛.中国材料工程大典第21卷[M].北京:化学工业出版社,2006:344-345. |
| [2] | 吴诗憞.金属超塑性变形理论[M].北京:国防工业出版社,1997:3-4. |
| [3] | Sherby O D;Walser B;Young C M.Super phstic ultrahigh carbon steels[J].Scripta Metall,1975(09):569-574. |
| [4] | E. Sato;S. Furimoto .Microstructure control for superplasticity of an ultra-high carbon steel[J].Materials Science Forum,1999(0):133-138. |
| [5] | Tomita Y;Okabayashi K.Improvement in lower temperature mechanical properties of 0.4 pct C-Ni-Cr-Mo ultrahigh strength steel with the second phase lower bainite[J].Metallurgical Transactions,1983(14A):485-492. |
| [6] | 杨超飞,邓晚平,薛钢,王任甫.10CrNi3MoV钢的超塑性行为[J].材料开发与应用,2013(06):5-8. |
| [7] | Spesis H J;Frommeyer G.Superplasticity behavior of rapidly solidified ultrahigh carbon tool steel X380CrVMo2593[J].Materials Science and Technology,1991(07):718-722. |
| [8] | 张寒,白秉哲.一种实现低合金超高强钢超塑变形的新思路[J].热处理,2012(02):24-27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%