研究了铬元素对X80抗大变形管线钢的微观结构和力学性能的影响.采用准静态拉伸试验,对其屈服强度、抗拉强度和伸长率进行测试;采用热膨胀法,在Gleeble-1500热模拟机上测定了两种试验钢的动态CCT曲线.结果表明:铬元素的添加降低了碳的活度,显著抑制了先共析铁索体的形成,提高了贝氏体转变温度,使钢的抗拉强度提高约40MPa,屈服强度基本不变,但使伸长率由19%降低到15%,-20℃冲击功由92J降低到52J.
参考文献
| [1] | 董玉华,余大涛,李鹤林.用于地震及地质灾害条件下的钢管性能研究进展[J].焊管,2008(04):14-16,20. |
| [2] | Shusuke Fujita;Izumi Takeuchi;Hidenori Shitamoto.Strain Capacity of X80 Grade Uoe Pipe for Strain Based Design in Seismic Area:International Seminar on X80 and Higher Grade Line Pipe Steel[A].China:China National Petroleum Corporation,2008 |
| [3] | 郑磊,高珊.高韧性针状铁素体X80级管线钢的试制[J].焊管,2005(02):21-24. |
| [4] | Zhenghua Tang;Waldo Stumpf .The role of molybdenum additions and prior deformation on acicular ferrite formation in microalloyed Nb-Ti low-carbon line-pipe steels[J].Materials Characterization,2008(6):717-728. |
| [5] | 汪瑞俊,杜晓东,孙国栋,王兰,王义飞,王家庆,丁厚福.铬含量对Cr-Ni-Mo系低碳合金钢组织性能的影响[J].热加工工艺,2007(08):15-17. |
| [6] | 吴成建;陈国良;强文江.金属材料学[M].北京:冶金工业出版社,2008 |
| [7] | 石川信行;鹿肉伸夫;近藤丈.超高强度高变形ヲイソバイブの开(凳)[J].JFE技报,2007(17):26. |
| [8] | 崔约贤;王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%