以丙烯酸酯类单体和有机氟单体(全氟烷基乙基丙烯酸酯,TEAc-N)为原料,采用溶液聚合的方式制备了阳离子型有机氟改性丙烯酸树脂并用其制成阴极电泳涂料.通过FT-IR、接触角仪、电导率仪等手段对共聚物树脂及其所配漆液与所得漆膜的性能进行表征,探讨了不同有机氟单体的添加量对电泳涂料性能的影响.结果表明:当有机氟单体的添加量(质量分数)为12％时,漆膜接触角达到了107.5°.改性后的阴极电泳涂料漆膜具有优良的耐腐蚀性.
参考文献
| [1] | 俎喜红,胡剑青,涂伟萍.新型阴极电泳涂料的研究进展[J].电镀与涂饰,2008(08):51-54. |
| [2] | Li H;Zhang ZB;Hu CP;Wu SS;Ying SK .Surface composition and property of film prepared with aqueous dispersion of polyurethaneurea-acrylate including fluorinated block copolymer[J].European Polymer Journal,2004(9):2195-2201. |
| [3] | R.Winter;P.G.Nixon;R.J.Terjeson;J.Mohtasham;G.L.Gard;N.R.Holcomb;D.W.Grainger;D.Graham;D.G.Castner .Perfluorinated polymer surfaces comprising SF_5-terminated long-chain perfluoroacrylate[J].Journal of Fluorine Chemistry,2002(2):107-113. |
| [4] | 周晓东,孙道兴,王凤英,李仓,滕艳.有机氟聚合物的应用研究进展[J].有机氟工业,2003(02):24-29. |
| [5] | 王韬,齐圣光,任碧野,朱雁,童真.含氟丙烯酸酯阴极电泳涂料的制备及防腐性能[J].华南理工大学学报（自然科学版）,2008(07):111-116. |
| [6] | DE WITTE J;PIESSENS G;DAMS H R .Fluorochemical intermediates,surfactants and their use in coatings[J].Surface Coatings International,1995,78(02):58,63-64. |
| [7] | 陈美玲,许丽敏,丁凡,杨莉,高宏.有机氟改性丙烯酸树脂的合成及研究[J].化工新型材料,2010(10):113-115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%