用真空液相烧结法在钢基体表面制备了TiC-Mo2FeB2系复合涂层,测定了TiC-Mo2FeB2系复合涂层-钢基体界面结合强度及界面结合区的显微硬度变化,研究了复合涂层的显微组织与界面微观结构和界面区元素分布。结果表明,涂层与钢基体之间具有较高的结合强度,当TiC含量为8%时结合强度最高为820.66 MPa,显微维氏硬度为12.06 GPa,在复合涂层-钢基体结合界面处,存在一个由涂层高硬度到钢基体低硬度的狭窄过渡区,并且两相之间形成了良好的冶金结合。
TiC-Mo2FeB2 composite cladding was prepared on steel substrate by vacuum liquid phase sintering.Bonding strength and micro-hardness between TiC-Mo2FeB2 composite cladding and steel substrate were measured,and microstructure of the composite cladding and elements distribution at interface were studied.The results show that the maximum bond strength is 820.66 MPa and micro Vickers hardness is 12.06 GPa when TiC content of the cladding is 8%.A transitional layer between the cladding and steel substrate with a good metallurgical bonding is observed.
参考文献
| [1] | 李国英.表面工程手册[M].北京:机械工业出版社,1997 |
| [2] | 李文虎,刘福田,冯小明.烧结温度对Mo2FeB2合金组织性能的影响[J].粉末冶金技术,2009(01):48-51,73. |
| [3] | 李文虎,徐峰,刘福田.铸渗法制备Mo2FeB2增强钢基表面复合材料[J].特种铸造及有色合金,2009(01):57-59. |
| [4] | Guo Chang-qing;Kelly P.M .Modeling of spatial distribution of the eutectic M2B borides in Fe-Cr-B cast irons[J].Journal of Materials Science,2004,39(03):1109-1111. |
| [5] | 石德珂;金志浩.材料力学性能[M].西安:西安交通大学出版社,1998 |
| [6] | 尤显卿,宋雪峰.WC/钢复合材料渗硼中WC颗粒对硼化物生长的影响[J].材料热处理学报,2006(03):121-126. |
| [7] | 周小平,胡心彬,高博,闫锋.反应烧结三元硼化物金属陶瓷覆层的组织与性能[J].金属热处理,2008(03):73-75. |
| [8] | 李文虎,徐峰,艾桃桃,冯小明.热处理对原位烧结合成Mo2FeB2陶瓷组织与性能的影响[J].材料热处理学报,2010(04):6-9. |
| [9] | 周细枝,周小平,潘永清.真空粉末烧结三元硼化物基金属陶瓷覆层的组织与性能[J].金属热处理,2005(12):48-50. |
| [10] | Schneider G A;Petzow G.Thermal Shock and Thermal Fatigue Behavior of Advanced Ceramics[M].Netherland:Klumer Academic Publishers,1993:269-278. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%