聚合物伸直链晶体一直是人们期望获得高强度、高模量材料中最引人注目的晶体结构,以往高压结晶获得聚合物伸直链晶体通常需要较高压力和温度的苛刻条件.本研究以液晶诱导制备含伸直链晶体的聚乙烯(PE)、聚酰胺(PA)及聚对苯二甲酸乙二醇酯(PET)等聚合物,使伸直链晶体的生成条件大幅度缓和.高压下液晶诱导生成聚合物伸直链晶体尝试成功,为其研究开辟了新的领域,同时也为聚合物伸直链晶体的工业化和实用化提供了新的途径和可能.文中同时介绍了液晶诱导聚合物伸直链晶体生成的两种机理,并提出了进一步研究的方向.
参考文献
| [1] | WARD I M.Mechanical Properties of Solid Polymer[J].Wiley Interscience,1971:7. |
| [2] | Geil P H;Anderson F R;Wunderlich B et al.[J].Journal of Polymer Science Part B:Polymer Physics,1964,2:3707. |
| [3] | Wunderlich B .[J].Journal of Polymer Science Part B:Polymer Physics,1969,7(12):2043-2050. |
| [4] | Bassett D C .[J].POLYMER,1976,17(06):460-470. |
| [5] | Maeda Y;Kanetsuna H .[J].Journal of Polymer Science,1976,14(12):2057-2072. |
| [6] | Rees D C;Bassett D C .[J].Journal of Polymer Science Part B:Polymer Physics,1971,9(03):385-406. |
| [7] | Nakafuku C;Polym .[J].Journal,1985,17(07):869-875. |
| [8] | Nakafuku C;Nakagawa H .[J].POLYMER,1991,32(04):696-702. |
| [9] | Crevecoeur G;Groeninckx G .[J].Polymer Engineering and Science,1990,30(09):532. |
| [10] | Tariq M M;Piekke J C .[J].Polymer Engineering and Science,1989,29(09):600. |
| [11] | 傅强 .[D].成都:成都科技大学,1993. |
| [12] | 傅强;黄锐;黄海 .[J].中国科学A辑,1994,24(11):1218-1224. |
| [13] | 李鹏 .[D].成都:四川大学,1999. |
| [14] | 吕云伟 .[D].成都:四川联合大学,1997. |
| [15] | 黄锐;黄海;吕云伟 et al.[J].功能高分子学报,1996,10(02):200-204. |
| [16] | 李良彬 .[D].成都:四川大学,2000. |
| [17] | Li L B;Li P;Huang R .[J].Journal of Materials Science Letters,1999,18:609-611. |
| [18] | Li LB.;Lu A.;Nie F.;Hong SM.;Wang CM.;Zhong YM.;Wang D.;Huang R. .High pressure crystallized poly(ethylene terephthalate): high crystallinity and large extended-chain crystals[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(18):6943-6947. |
| [19] | Li LB.;Huang R.;Fan WY.;Hong SM.;Wang G.;Zhong YM.;Zhang L. .Electron microscopy of high-pressure crystallized poly(ethylene terephthalate)[J].Journal of Polymer Science, Part B. Polymer Physics,2000(12):1612-1616. |
| [20] | Li L B;Huang R;Zhang L et al.[J].Polymer,2001,42:2085-2089. |
| [21] | Li L B;Huang R;Hong S M .[J].Journal of Materials Science Letters,2001,807-809 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%