根据波音737CL飞机龙骨梁ADF环形天线组件固定孔区域的剥蚀特征,采用有限元分析和盐雾环境暴露试验研究了正应力在剥蚀中的作用.结果表明,纵向L方向及长横向LT方向压应力可加速7150铝合金的剥蚀的形成和扩展;L方向、LT方向拉应力以及短横向ST方向压应力抑制合金的剥蚀的形成和扩展.
Based on an investigation of the exfoliation corrosion（EFC） evolution around ADF antenna installing holes on aluminum alloy 7150-T77511 keel beam for aircraft B737CL,the effect of axial stress on the EFC was studied by means of finite element analysis and corrosion test in salt fogging environment.The results showed that compressive stress along directions L and LT accelerated EFC,whilst tensile stress along directions L and LT,and compressive stress along direction ST retarded EFC.
参考文献
| [1] | Boeing Industry. 73%300/400/500 Structure Repair Manual[S]. Seattle: 2009. |
| [2] | 中国民用航空局.航空器结构持续完整性大纲ACl21-65[S].北京:2005. |
| [3] | 黄昌龙,万小朋.波音737CL龙骨梁BS535区域腐蚀规律[J].南昌航空工业学院学报(自然科学版),2010,24(3):39. |
| [4] | Robinson M J, Jackson N C. The influence of grain struc- ture and intergranular corrosion rate on exfoliation and stress corrosion cracking of high strength A1-Cu-Mg al- loys[J]. Corros. Sci., 1999, 41(5): 1013. |
| [5] | Kelly D J, Robinson M J. Influence of heat treatment and grain shape on exfoliation corrosion of A1-Li alloy 8090[J]. Corrosion, 1993, 49(10): 787. |
| [6] | 戴晓元,夏长清,孙振起等.A1-9.0Zn-2.5Mg-1.2Cu-0.12Sc-O.15Zr合金的组织和性能[J].中国有色金属学报,2007.17(3):396. |
| [7] | 张新明,张小艳,刘胜胆等.固溶后降温预析出对7A55铝合金力学及腐蚀性能的影响[J].中南大学学报,2007,38(5):789. |
| [8] | McNaughtan D, Worsfold M, Robinson M J. Corrosion product force measurements in the study of exfoliation and stress corrosion cracking in high strength aluminum alloys[J]. Corros. Sci., 2003, 45(10): 2377. |
| [9] | Robinson M J. Mathematical modeling of exfoliation cor- rosion in high strength aluminum alloys[J]. Corros. Sci., 1982, 22(8): 775. |
| [10] | Robinson M J. The role of wedging stresses in the exfolia- tion corrosion of high strength aluminum alloy[J]. Corros. Sci., 1983, 23(8): 887. |
| [11] | Zhao X, Frankel G S. Effects of relative humidity, temper and stress on exfoliation corrosion kinetics of AA7178[J]. Corros. Sci., 2006, 62(11): 956. |
| [12] | Boeing Industry. 737-300/400/500 Airplane Maintenance Manual[S]. Seattle: 2009. |
| [13] | Boeing Industry. Boeing Material Specification BMS7- 257[S]. Seattle: 1993. |
| [14] | 单祖辉.材料力学[M].北京:高等教育出版社,1999. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%