根据C-Si-Mn-Cr-Nb试验钢的双道次变形和分段冷却热模拟试验结果,进行了试验钢控轧控冷试验,分析了工艺参数对试验钢组织和性能的影响,获得了具有不同力学性能的铁索体+马氏体或铁素体+贝氏体双相组织.结果表明,试验钢两段轧制分段冷却后550℃卷取获得铁素体+马氏体双相组织,屈服强度415 MPa,抗拉强度710 MPa,伸长率23.0%,屈强比0.59.500℃卷取得到铁素体加粒状贝氏体双相组织,与550℃卷取相比,屈服强度升高35 MPa,抗拉强度降低45 MPa,伸长率略微降低.
参考文献
| [1] | 敖炳秋.轻量化汽车材料技术的最新动态[J].汽车工艺与材料,2002(08):1-21,105. |
| [2] | 马鸣图,M.F.Shi.先进的高强度钢及其在汽车工业中的应用[J].钢铁,2004(07):68-72. |
| [3] | Hyun D I;Oak S M;Kang S S.Estimation of Hole Flange Ability for High Strength Steel Plates[J].Journal of Materials Processing Technology,2002(130-131):9. |
| [4] | Hong SC.;Lee KS. .Influence of deformation induced ferrite transformation on grain refinement of dual phase steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):148-159. |
| [5] | Cosmo De M;Galantucci L M;Tricarico L.Design of Process Parameters for Dual Phase Steel Production With Strip Rolling Using the Finite-Element Method[J].Journal of Materials Processing Technology,1999(92-93):486. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%