用热重及热-质联用测定紫外光固化后的甲基丙烯酰氧丙基笼型倍半硅氧烷(MPA-POSS)的热分解过程,采用Ozawa法、Kissinger-Akahira-Sunose (KAS)法和Friedman法对其热降解动力学进行分析.样品的分解过程主要分为两个阶段,初期主要是羰基和C-O键的断裂,在347～677℃范围内产生CO和CO2,在445～655℃范围内产生CH+3.分解活化能在119.88～133.72kJ/mol之间,反应级数为n=0.852.
参考文献
| [1] | Deng S F;Wang C F;Zhou Y .[J].Materials Science and Engineering,2008,477:96-99. |
| [2] | Macan J;Brnardic I;Orlic S et al.[J].Polymer Degradation and Stability,2006,91:122-127. |
| [3] | 刘佳,李顺祥,贾树盛.LLDPE/EVA/ZnO纳米复合材料的制备与BP-Markov性能预测研究[J].功能材料,2009(11):1925-1928. |
| [4] | 王川,邢哲,夏延致,隋坤艳,纪全,孔庆山.多壁碳纳米管的处理及其在芳纶1313中的分散[J].功能材料,2009(02):325-327. |
| [5] | Yu H;Ren W;Zhang Y .[J].Journal of Applied Polymer Science,2009,113:17-23. |
| [6] | Edward T K;Gareth H M;Robert E C .[J].Polymer,2006,47:299-309. |
| [7] | Gao J G;Dong C F;Du Y G .[J].International Journal of Polymeric Materials,2010,59:1-14. |
| [8] | 斋藤宏;矶崎正义;安藤秀树 .具有官能团的笼型倍半硅氧烷类树脂及其制造方法[P].JP:(31)2002-285387,2004-06-16. |
| [9] | Friedman H L .[J].Journal of Polymer Science Part C:Polymer Letters,1964,6:183-195. |
| [10] | Kissinger H E .[J].Analytical Chemistry,1957,29:1702-1706. |
| [11] | Doyle C D .[J].Journal of Applied Polymer Science,1961,5:285-292. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%