采用循环极化曲线测试、慢应变速率拉伸试验,结合扫描电镜观察研究了在钨极氩弧焊的保护气体中加入2％氮气对2205双相不锈钢焊接接头的相比例、点蚀和应力腐蚀开裂敏感性的影响.结果表明,虽然焊接导致材料中γ相含量降低,点蚀和应力腐蚀的敏感性增大,但与100％氩气的保护气体相比,加入2％氮气后促进了γ相转变,使焊接接头两相比例接近于母材,并使焊接对点蚀和应力腐蚀的不利影响受到有效抑制.
参考文献
| [1] | R. Badji;B. Bacroix;M. Bouabdallah .Texture, microstructure and anisotropic properties in annealed 2205 duplex stainless steel welds[J].Materials Characterization,2011(9):833-843. |
| [2] | 龚利华,张波,王赛虎.超级双相不锈钢焊接接头的耐蚀性能[J].焊接学报,2010(07):59-62. |
| [3] | 龚利华,程东亮,张波.电化学法分析超级双相不锈钢焊接接头的耐点蚀性[J].腐蚀科学与防护技术,2010(06):521-525. |
| [4] | ASTM E562.Standard test method for determining volume fraction by systematic manual point count[S]. |
| [5] | V. S. Mourn;L. D. Lima;J. M. Pardal .Influence of microstructure on the corrosion resistance of the duplex stainless steel UNS S31803[J].Materials Characterization,2008(8):1127-1132. |
| [6] | 宋志刚,陈斌,郑文杰,雷德江,程士明.固溶温度对00Cr22Ni5Mo3N钢组织及耐点蚀性能的影响[J].钢铁研究学报,2007(06):69-71,98. |
| [7] | Effect of thermal cycles on the corrosion and mechanical properties of UNS S31803 duplex stainless steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(12):2969. |
| [8] | 刘雄,何燕霖,丁秀平,宋红梅,胡锦程,陈旭,李麟.高温时效对2205双相不锈钢中σ相析出行为的影响[J].材料热处理学报,2010(03):48-51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%