采用称重法研究了油井釆出液成分与温度对Q235钢腐蚀行为的影响;运用极化曲线和滞后环等电化学方法结合SEM和XRD等方法,研究了Q235钢的腐蚀机理.结果表明:采出液中Cl-、SO2-4对腐蚀速率影响较大,而HCO-3、Ca2+影响较小,随着Cl-、SO2-4浓度的增大试验钢的腐蚀速率增大;随着HCO3-3浓度的增大试验钢的腐蚀速率先增大后减小;Ca2+浓度很小时,对试验钢的腐蚀速率没有明显的影响,但当Ca2+质量浓度达到240 mg·L-1时,腐蚀速率迅速降低;在80℃之前,试验钢的腐蚀速率随温度升高而加快;试验钢的腐蚀机理为垢下腐蚀.
参考文献
| [1] | M.Salman;H.Qabazard;M.Moshfeghian .Water scaling case studies in a Kuwaiti oil field[J].Journal of Petroleum Science & Engineering,2007(1/2):48-55. |
| [2] | Migahed MA .Corrosion inhibition of steel pipelines in oil fields by N,N-di(poly oxy ethylene) amino propyl lauryl amide[J].Progress in Organic Coatings: An International Review Journal,2005(2):91-98. |
| [3] | M. A. Migahed;I. F. Nassar .Corrosion inhibition of Tubing steel during acidization of oil and gas wells[J].Electrochimica Acta,2008(6):2877-2882. |
| [4] | M.A. Deyab .Effect of cationic surfactant and inorganic anions on the electrochemical behavior of carbon steel in formation water[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(5):2315-2328. |
| [5] | 万里平,孟英峰,王存新,杨龙.西部油田油管腐蚀结垢机理研究[J].中国腐蚀与防护学报,2007(04):247-251. |
| [6] | 廖作才,LIN Bao-qin,张继春.油气井生产中的腐蚀与防护[J].商品储运与养护,2008(06):115-116. |
| [7] | 廖作才,LIN Bao-qin,张继春.油气井生产中的腐蚀与防护[J].商品储运与养护,2008(06):115-116. |
| [8] | 陈新萍,高清河,许景秋.大庆杏北油田腐蚀因素研究[J].化学与黏合,2006(04):279-281. |
| [9] | 唐聿明,张琳,左禹.几种阴离子对A3钢在NaHCO3+NaCl溶液中亚稳态孔蚀行为的影响[J].腐蚀科学与防护技术,2005(05):307-310. |
| [10] | 黄凯锋,刘文君.北京某水厂模拟管网内部腐蚀特性分析[J].中国给水排水,2007(13):63-65. |
| [11] | 赵锋洛.胡状油田腐蚀与防护现状研究[J].全面腐蚀控制,2003(05):6-11. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%