本文研究了过程控制剂的添加量对SiO_2-Al复合粉出粉率的影响及球磨时间对粉末的细化和固相反应温度的影响.应用激光粒度仪、扫描电镜、X射线衍射仪和差热分析仪对球磨后的复合粉进行分析.研究表明,经20 h球磨时,过程控制剂的添加量为4%时,出粉率高达85%;随着球磨时间的延长,SiO_2-Al复合粉被逐渐细化,20 h球磨后,其中位径降至4.35 μm,但是并没有发生固相反应;随着球磨时间的延长,降低了SiO_2和Al的固相反应温度.
The impact of process control agent addition on the extraction rate and the milling time on the powders refinement, mechanical alloying and thermal stability of SiO_2-Al composite powders were studied in this paper. The composite powders after milling were analyzed by laser particle size analyzer, scanning electron microscopy, X-ray diffraction and differential thermal analyzer. The result showed that by 20 h of milling, the extraction rate of composite powders was up to 85% with adding 4% of the process control agent. With the extension of milling time, SiO_2-Al composite powders have been gradually refined, median diameter down to 4.35 μm after 20 h milling, but there is no reaction occurred. The temperature of reaction has been fallen with the extension of milling time.
参考文献
| [1] | Zhou X B;De Hosson J Th M .A reaction coating on aluminium alloys by laser processing[J].Reaction Coating,1993,28(02):219-224. |
| [2] | Zhou X B;De Hosson J Th M .Microstructure and interfaces of a reaction coating on aluminium alloys by laser processing[J].Journal of De Physique IV,1993,3:1007-1009. |
| [3] | 陈新亮 .机械合金化Al/Ti混合粉末的组织和热稳定性研究[D].天津大学,2004. |
| [4] | 方景 .反应合成Al_2O_3颗粒增强铝基复合材料的研究[D].镇江:江苏大学,2008. |
| [5] | 赖金权,王蕾,许伯藩,杜甍,朱宏才.过程控制剂在高能球磨法制备SiC/Al复合粉末中的作用研究[J].武汉科技大学学报（自然科学版）,2007(01):20-22. |
| [6] | Ruiz-Navas E M;Fogagnolo J B;Velasco F .Onestep production of aluminum matrix composite powders by mechanical alloying[J].Applied Science and Manufacturing,2004,37(11):2114-2120. |
| [7] | 江巍 .氮气氛条件下氧化铝及铝的机械力化学效应研究[D].南京工业大学,2006. |
| [8] | 贾建刚,马勤,周琦,季根顺,郭铁明.3Fe/Al混合粉末的高能球磨及环境介质的相互作用[J].材料热处理学报,2007(06):11-13. |
| [9] | Li F;Wu B Y .Mechanical alloying-a new technology of alloying in solid state[J].Materials For Mechanical Engineering,1999,23(04):22. |
| [10] | 毛松科 .机械球磨固相化学反应合成及其放氢性能研究[D].兰州:兰州理工大学,2008. |
| [11] | 罗成,张红霞,杨明,胡树兵,涂江平.Al-ZnO反应球磨制备Zn/Al2O3复合粉末研究[J].粉末冶金技术,2006(03):209-212. |
| [12] | Huang B L;Perez R J;Lavernia E J .Formation of su-persaturated solid solutions by mechanical alloying[J].Nano-Structured Materials,1996,7(01):67-79. |
| [13] | Suwa Y;Inabaki M;Naka S .Polymorphis tranformation of titaniym dioxide by mechanical grindding[J].Journal of Materials Sciety,1984,17(19):1397-1405. |
| [14] | 席生岐,屈晓燕,刘心宽,马明亮,周敬恩,王笑天.高能球磨固态扩散反应研究[J].材料科学与工艺,2000(03):88-91. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%