研究硫酸电解液中添加己二酸铵对7075-T6铝合金阳极氧化的影响,采用场发射扫描电子显微镜(FE-SEM)对7075-T6铝合金在不添加和添加己二酸铵的硫酸电解液中制备的阳极氧化膜表面的微观形貌进行分析,采用线性阳极极化研究7075-T6铝合金在两种电解液中的极化行为.利用动电位极化技术和电化学阻抗谱(EIS)研究两种电解液中制备的阳极氧化膜的耐腐蚀性能.结果表明:硫酸电解液中添加己二酸铵可以通过降低电流密度来改善氧化膜的结构,减少氧化膜缺陷,降低微孔孔径,提高阻挡层厚度,从而降低氧化膜的自腐蚀电流密度,提高氧化膜耐腐蚀性能.
参考文献
| [1] | BIRBILIS N;CAVANAUGH M K;BUCHHEIT R G .Electrochemical behavior and localized corrosion associated with A17Cu2Fe particles in aluminum alloy 7075-T651[J].Corrosion Science,2006,48(12):4202-4215. |
| [2] | Guillaumin V.;Mankowski G. .Localized corrosion of 6056 T6 aluminium alloy in chloride media[J].Corrosion Science,2000(1):105-125. |
| [3] | GUILLAUMIN V;MANKOWSKI G .Localized corrosion of 2024 T351 aluminium alloy in chloride media[J].Corrosion Science,1999,41(03):421-438. |
| [4] | Weilong Zhang;G. S. Frankel .Transitions between pitting and intergranular corrosion in AA2024[J].Electrochimica Acta,2003(9):1193-1210. |
| [5] | EARL G .Chromium[J].Metal Finishing,1997,95(03):59-61. |
| [6] | Moutarlier V.;Gigandet MP.;Pagetti J.;Ricq L. .Molybdate/sulfuric acid anodising of 2024-aluminium alloy: influence of inhibitor concentration on film growth and on corrosion resistance[J].Surface & Coatings Technology,2003(1):87-95. |
| [7] | V. Moutarlier;M.P. Gigandet;J. Pagetti;S. Linget .Influence of molybdate species added to sulphuric acid on composition and morphology of the anodic layers formed on 2024 aluminium alloy[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2005(1/2):197-204. |
| [8] | MOUTARLIER V;GIGANDET M P;NORMAND B;PAGETTI J .EIS characterisation of anodic films formed on 2024 aluminium alloy in sulphuric acid containing molybdate or permanganate species[J].Corrosion Science,2005,47(04):937-951. |
| [9] | 刘忆,刘凤霞.工业纯铝硬质阳极氧化的工艺研究[J].表面技术,2006(06):35-36,47. |
| [10] | M. Curioni;P. Skeldon;E. Koroleva .Role of Tartaric Acid on the Anodizing and Corrosion Behavior of AA 2024 T3 Aluminum Alloy[J].Journal of the Electrochemical Society,2009(4):C147-C153. |
| [11] | WONG Chun-ming;MOJI Y .Method for anodizing aluminum:[P].United States Patent,4894127,1990-01-06. |
| [12] | Sachiko Ono;Chieko Wada;Hidetaka Asoh .Structure and property of anodic barrier films formed on aluminum in low voltage range[J].Electrochimica Acta,2005(25/26):5103-5110. |
| [13] | 李永星,于美,刘建华,李松梅,陈高红.电压加载下己二酸铵对2024-T3铝合金阳极氧化膜的封闭研究[J].航空学报,2011(07):1326-1335. |
| [14] | ZHOU X;THOMPSON G E;SKELDON P;WOOD G C SHIMIZU K HABAZAKI H .Anodic oxidation of an AI-2wt%Cu alloy:Effect of grain orientation[J].Corrosion Science,1999,41(06):1089-1094. |
| [15] | 刘建华,李明,李松梅,詹中伟.挤压成型对LC4CS铝合金棒材阳极氧化膜结构的影响[J].航空学报,2009(02):368-373. |
| [16] | LIU Jian-hua;LI Ming;LI Song-mei;HUANG Min .Effect of microstructure of anodic oxide formation in sulfuric acid[J].International Journal of Minerals Metallurgy and Materials,2009,16(04):432-438. |
| [17] | M. Saenz de Miera;M. Curioni;P. Skeldon;G.E. Thompson .Modelling The Anodizing Behaviour Of Aluminium Alloys In Sulphuric Acid Through Alloy Analogues[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(12):3410-3415. |
| [18] | The behaviour of second phase particles during anodizing of aluminium alloys[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(7):2489. |
| [19] | M. Curioni;M. Saenz de Miera;P. Skeldon .Macroscopic and Local Filming Behavior of AA2024 T3 Aluminum Alloy during Anodizing in Sulfuric Acid Electrolyte[J].Journal of the Electrochemical Society,2008(8):(C)387-395. |
| [20] | M. Curioni;P. Skeldon;G. E. Thompson .Anodizing of Aluminum under Nonsteady Conditions[J].Journal of the Electrochemical Society,2009(12):407-413. |
| [21] | Houser JE;Hebert KR .Modeling the potential distribution in porous anodic alumina films during steady-state growth[J].Journal of the Electrochemical Society,2006(12):B566-B573. |
| [22] | Gregory Boisier;Nadine Pebere;Catherine Druez .FESEM and EIS Study of Sealed AA2024 T3 Anodized in Sulfuric Acid Electrolytes: Influence of Tartaric Acid[J].Journal of the Electrochemical Society,2008(11):(C)521-529. |
| [23] | S.J. Garcia-Vergara;K. El Khazmi;P. Skeldon;G.E. Thompson .Influence of copper on the morphology of porous anodic alumina[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(10):2937-2946. |
| [24] | L. Iglesias-Rubianes;S. J. Garcia-Vergara;P. Skeldon;G. E. Thompson;J. Ferguson;M. Beneke .Cyclic oxidation processes during anodizing of Al-Cu alloys[J].Electrochimica Acta,2007(24):7148-7157. |
| [25] | Corrosion evaluation of microarc oxidation coatings formed on 2024 aluminium alloy[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2010(8):P.2687. |
| [26] | KEVIN D;DOBSON;JAMES MC QUILLAN A .In situ infrared spectroscopic analysis of the adsorption of aliphatic carboxylic acids to TiO2,ZrO2,A12O3 and Ta2O5 from aqueous solutions[J].Spectrochimica Acta Part A:Molecular and Biomolecular Spectroscopy,1999,55(7/8):1395-1405. |
| [27] | LANDRY C C;PAPP(E) N;MASON M R;APBLETT A W TYLER A N MACINNES A N BARRON A R .From minerals to materials:Synthesis of alumoxanes from the reaction of boehmite with carboxylic acids[J].Journal of Materials Chemistry,1995,5(02):331-338. |
| [28] | SUAY J J;GIMENEZ E;RODRIGUEZ T;HABBIB K SAURA J J .Characterization of anodized and sealed aluminium by EIS[J].Corrosion Science,2003,45(03):611-624. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%