不同甘油质量分数的添加剂对浸没沉淀相转化法制备聚偏氟乙烯（PVDF）微孔膜的结构及性能具有显著影响。实验结果表明,铸膜液中甘油质量分数越高,在相同的制膜条件下,铸膜液越容易发生凝胶分相,所成膜表面越发致密,孔密度降低,断面指状大孔的长度和胞腔状结构的相互贯通性增加。另外膜的空隙率均随着铸膜液中甘油质量分数的增加而增加,膜的平均孔径则当甘油质量分数为5%时达到最大,从所制得膜的膜蒸馏性能来看,在添加剂质量分数为8%的范围内,膜蒸馏通量和截留率的基本趋势是随着铸膜液中甘油质量分数的增加而上升。
Different contents of glycerol as additives have great influence on morphology and performance of polyvinylidene fluoride（PVDF） membranes prepared via immersion precipitation phase inversion technique.The results show that,the more glycerol contents added,the easier of gel phase demixing occurs in the dopes.Moreover,with the increase of the glycerol contents,the morphology of the top surface becomes densed.On the cross section of the prepared membrane,the length of the finger-like pores becomes larger and the connectivity of the globule-like pores becomes better.Within glycerol mass fraction 8%,the general performances of the prepared membrane,for example,the porosity,the flux and rejection of membrane distillation,are all increase with the increase of glycerol contents in dopes,while the mean pore size of the prepared membrane reaches the maximum when glycerol mass fraction is 5%.
参考文献
| [1] | Yeow ML.;Liu YT.;Li K. .Morphological study of poly(vinylidene fluoride) asymmetric membranes: Effects of the solvent, additive, and dope temperature[J].Journal of Applied Polymer Science,2004(3):1782-1789. |
| [2] | 陆茵,陈欢林,李伯耿.溶剂浓度对PVDF相转换膜大孔结构的影响[J].高分子学报,2003(06):852-857. |
| [3] | Wang XY;Zhang L;Sun DH;An QF;Chen HL .Effect of coagulation bath temperature on formation mechanism of poly(vinylidene fluoride) membrane[J].Journal of Applied Polymer Science,2008(3):1656-1663. |
| [4] | Xuyun Wang;Lin Zhang;Dahai Sun .Formation mechanism and crystallization of poly(vinylidene fluoride) membrane via immersion precipitation method[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2009(1/3):170-178. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%