通过对718合金中沉淀强化元素Al,Ti以及固溶强化元素W含量的调整,研究了δ相形成规律及合金中γ＂/γ′复合析出组织的形成条件,同时分析了合金的微观组织与力学性能之间的关系.结果表明,维持理想的(Al+Ti+Nb)含量(at%)及(Al+Ti)/Nb原子分数比可以显著减少针状δ相的析出,得到稳定的γ＂/γ′复合析出组织并提高合金的拉伸强度、持久及硬度等多项力学性能.而在718合金基础上,采用W强化的合金与原型718合金相比也显现出了更为优异的力学性能.
参考文献
| [1] | Cozar R;Pineau A .[J].Metallurgical and Materials Transactions,1973,4:47. |
| [2] | Barker J F;Ross E W;Radavich J F.[J].Journal of Metals,1970(01):31. |
| [3] | Schafrik R E;Ward D;Grod R.[A].Warrendale:The Mineral,Metals and Materials Society,2001:1. |
| [4] | Radavich J F;Fort A.[A].Warrendale:The Mineral,Metals and Materials Society,1994:635. |
| [5] | 谢锡善;董建新;陈卫 et al.[J].金属热处理学报,1997,18(03):37. |
| [6] | Xie X S.[A].Warrendale:The Mineral,Metals and Materials Society,2005:269. |
| [7] | Cao W D.[A].Warrendale:The Mineral,Metals and Materials Society,2005:165. |
| [8] | Rosier J;Evans A G .[J].Materials Science and Engineering A,1992,153(1-2):438. |
| [9] | Chen W;Chaturvedi M C.[A].Warrendale:The Mineral,Metals and Materials Society,1994:567. |
| [10] | 李树祺.GH169合金显微组织对合金裂纹扩展速率的影响[J].材料工程,1998(05):26. |
| [11] | Manriquez J A;Bretz P L;Rabenberg L.[A].Warrendale:The Mineral,Metals and Materials Society,1992:507. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%