Bright long afterglow phosphorescence glasses were prepared by using SrAl2O4 : Eu2+, Dy3+ phosphors and suitable glass frits together. The SrAl2O4: Eu2+,Dy3+ phosphors were initially prepared by the solid reaction method. Three kinds of glass frits were prepared to match the SrAl2O4: Eu2+,Dy3+ phosphors. Effects of the compositions of the glass frits, the ratios of the phosphors to the frits as well as the firing temperature and firing times on the properties of the samples were discussed. XRD analysis indicated the samples exhibited the typical diffraction peaks of SrAl2O4:Eu2+, Dy3+. The emission spectra of the samples showed broad bands peaking at 510nm. The excitation spectra of the samples showed broad bands ranging from 300 to 480nm. These are believed due to the 5d4f-4f transitions of Eu2+ in the SrAl2O4: Eu2+, Dy3+ phosphors. The afterglow luminescence of the samples excited by a 40W fluorescence lamp for 30min can be observed in the dark for more 10h with the naked eyes. It can find wide applications in many fields.
参考文献
| [1] | T Matsuzawa;Y Aoki;N Takeuchi;Y Morayama .[J].Journal of the Electrochemical Society,1996,143:2670. |
| [2] | T Katsumata;T Nabae;K Sasajima .[J].Journal of the Electrochemical Society,1997,144(09):243. |
| [3] | Y Murazaki;K Arai;K Ichinomiya .[J].Japan Rare Earth,1999,35:41. |
| [4] | E Nakazawa;T Mochida .[J].Journal of Luminescence,1997,72-74:236. |
| [5] | X Y Zhang;G Cheng;X Y Mi;Z Y Xiao,W W Jiang,J J Hu .[J].Journal of Rare Earths,2004,22(01):137. |
| [6] | X Y Zhang;Z H Bai;X C Wang;W Z Wang,H Z Sun,X Guan,Z F Chao,J X Du,G Xu,Y Guo .[J].J Wuhan Univ of Tech,2002,24(09):8. |
| [7] | X Y Zhang;Y Guo;Z H Bai;X R Wang,Z F Chao .[J].Mater Sci Technol,2002,10(03):314. |
| [8] | 张希艳,柏朝晖,关欣,王晓春,王伟忠,孙宏志,曹志峰,杜锦秀,郭瑜.SrAl2O4：Eu2+ ,Dy3+长余辉光致发光材料的固相反应法合成与特性[J].稀有金属材料与工程,2003(05):379-382. |
| [9] | W Y Jia;H B Yuan .[J].Journal of Luminescence,1999,83-84:465. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%