利用空心阴极烧结工艺制备了SiCp/Ti基复合材料,研究了铝含量对复合材料组织和性能的影响。结果表明:铝的加入并未使复合材料形成新相,但可以促进烧结和Ti3SiC2相的形成;随着铝含量的增多,复合材料的致密度一直降低,而抗弯强度和硬度均呈先降低后上升再降低的趋势;当铝的体积分数为6%时,材料的相对密度为92.5%,抗弯强度为400MPa,硬度为54HRC。

SiC particles reinforced Ti matrix composites were prepared using the hollow cathode plasma sintering. The effect of A1 content on the microstructure and properties of the composites was investigated. The results show that no new phase formed in the composites after adding of A1, but could improve the sintering and the formation of Ti3SiC12 phase. With the increase of A1 content, the density of the composites decreased, both the bending strength and hardness decreased firstly, then increased and finally decreased. When the A1 content was 6vol% , the relative density, bending strength and hardness of the composites were about 92. 5%, 400 MPa and 54 HRC.

参考文献

[1] 毛小南,赵永庆,杨冠军.国外航空发动机用钛合金的发展现状[J].稀有金属快报,2007(05):1-7.
[2] 梅运旺,杨延清,罗贤,李健康,马志军,陈彦.SiC纤维增强Ti600复合材料界面研究[J].稀有金属材料与工程,2008(10):1839-1843.
[3] 吕祥鸿,杨延清,马志军,陈彦.SiC连续纤维增强Ti基复合材料界面反应扩散研究进展[J].稀有金属材料与工程,2006(01):164-168.
[4] ZhengMing Sun;Songlan Yang;Hitoshi Hashimoto .Effect of Al on the synthesis of Ti_3SiC_2 by reactively sintering Ti-SiC-C powder mixtures[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):321-325.
[5] 望军,刘颖,叶金文,涂铭旌.Ti(C,N)基金属陶瓷抗弯强度的研究[J].硬质合金,2008(03):140-142.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%