采用高速火焰(HVOF)热喷涂工艺制备了金属间化合物NiAl-Ta-Cr涂层.研究了喷涂距离、氧气流量以及燃气流量等工艺参数对涂层组织结构和性能的影响.用光学显微镜观察涂层的组织结构并测定涂层的孔隙率,用LECOTC316气体抽提仪检测涂层的氧含量.结果表明,氧气流量、喷涂距离等工艺参数对涂层性能的影响比较明显.随着喷涂距离的增加,涂层的氧含量降低;O/H比率越大,涂层的氧含量越高,而孔隙率降低,沉积率越高.涂层经1100℃,4 h真空热处理后,变得更加均匀和致密,孔隙率降低,但涂层的硬度有所降低.涂层经1100℃,100 h高温氧化处理后,在涂层表面生成了连续的氧化铝氧化层,硬度比真空退火后略有下降.
参考文献
| [1] | SauthoffG;Zeumer B .[P].US 5935349,1999. |
| [2] | Zeumer B;Sauthoff G .[J].Intermetallics,1998,6:451. |
| [3] | Palm M;Preuhs J;Sauthoff G .[J].Journal of Materials Processing Technology,2003,136:105. |
| [4] | Palm M;Preuhs J;Sauthoff G .[J].Journal of Materials Processing Technology,2003,136:114. |
| [5] | Hearley J A;Little J A;Sturgeon A J .[J].Surface and Coatings Technology,2000,123:210. |
| [6] | Zhao Lidong;Lugscheider Erich .[J].Surface and Coatings Technology,2002,149:231. |
| [7] | Wang Y;Chen W .Microstructures, properties and high-temperature carburization resistances of HVOF thermal sprayed NiAl intermetallic-based alloy coatings[J].Surface & Coatings Technology,2004(1):18-28. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%