用极化曲线、失重和EIS等方法研究了AMT(2-氨基-5-巯基-1,3,4-噻二唑)在碳钢/5%HCl体系中的缓蚀行为和机理.研究表明AMT在该体系中表现为混合型缓蚀剂,其缓蚀机理可归因于几何覆盖效应,在电极表面的吸附符合Langmuir吸附等温式,吸附热约为27.10kJ/mol左右,其EIS图谱在自腐蚀电位下与空白一样,只有一个时间常数,但一定程度阴极极化时出现低频吸附容抗
The inhibition behavior of AMT(2 amino 5 mercapto 1,3,4 thiadiazole) in the carbon steel/5%HCl system was studied by polarization curve,weight loss and EIS. It was found that AMT acted as a mix type inhibitor and its inhibiting on effect was due to the ge
参考文献
| [1] | GajendragadMR,AgarwalaU．IndianJ．Chem．,1975,13:13312BastidasJM,OteroE．Werks．Koros．,1996,47(6):3333GanorkarMC,PanditRaoV,GayathriP,etal．Stud．inCons．,1988,33:974OsamMM,KhamisEandMichealA．Coros．Prev．andControl,1994,41(3):605OsamMM,KhamisE,MichealA．Anti-CorosionMethodsandMaterials,1994,41(2):36DonnelyB,DownieT,GrzeskowiakR,etal．Coros．Sci．,1978,18(2):1097曹楚南．腐蚀电化学．北京:化学工业出版社,1994,1338曹楚南．材料保护,1990,23(1-2):409CAOChu′nan．ElectrochimicaActa,1990,35(5):83F |