采用极化曲线技术和扫描电镜结合能谱分析，对供货状态和打磨光滑状态的钢筋在混凝土氯离子侵蚀过程中的腐蚀行为进行了研究。通过不同浸泡时间，试样获得了不同的自腐蚀电位及自腐蚀电流密度，分析了不状态试样的表面形貌。结果表明，由于钢筋表面状态不同，钢筋在混凝土中的不同阶段表现出不同的电化学行为。在初期无氯离子的条件下，不同表面状态的钢筋表面钝化膜的稳定性不同，而随着氯离子在混凝土中的入侵，两种钢筋的腐蚀速率也存在很大的差异。结合表面状态分析表明，供货状态钢筋在混凝土氯离子入侵过程中比打磨光滑状态钢筋更易发生腐蚀。
The corrosion behavior of reinforced steel with different surface states in steel bar immersed in simulated solution containing Cl- was investigated by electrochemical measurements,scanning electron microscopy with energy dispersive X-ray spectrometer (SEM/EDX).The changes of corrosion potential and corrosion current density of reinforced steel with the immersion time were obtained,and the morphology of samples with different surface states was analyzed.The results show that the corrosion behavior of reinforced concrete was different in different immersion stages.The stability of passive film formed on the polished steel was better than that of as-supplied steel at the initial stage was when Cl- did not reach the surface of steel.The corrosion rate of as-supplied steel was larger than that of polished steel with the increase of Cl- ions on the surface of steel due to the rough surface caused by thermal oxidation in manufacture process.
参考文献
| [1] | 王立成.氯盐环境条件下混凝土氯离子侵蚀模型及其研究进展[J].水运工程,2004(04):5-9. |
| [2] | 王胜年.我国海港工程混凝土耐久性技术发展及现状[J].水运工程,2010(10):1-7,118. |
| [3] | 范宏,付燕弟,赵铁军.暴露21年后混凝土的碳化及氯离子侵入研究[J].工业建筑,2011(05):14-18,38. |
| [4] | 李春秋,李克非.干湿交替下表层混凝土中氯离子传输：原理、试验和模拟[J].硅酸盐学报,2010(04):581-589. |
| [5] | K. Thangavel;N. S. Rengaswamy .Relationship between Chloride/hydroxide Ratio and Corrosion Rate of Steel in Concrete[J].Cement & concrete composites,1998(4):283-292. |
| [6] | Ki Yong Ann;Ha-Won Song .Chloride threshold level for corrosion of steel in concrete[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(11):4113-4133. |
| [7] | P. V. Nygaard;M. R. Geiker .A method for measuring the chloride threshold level required to initiate reinforcement corrosion in concrete[J].Materials and structures,2005(278):489-494. |
| [8] | 俞海勇,张贺,王琼,徐强,邓咏梅.海工混凝土钢筋锈蚀速率预测模型研究[J].建筑材料学报,2009(04):478-481,492. |
| [9] | 刘晓敏,史志明,许刚,宋光铃,林海潮,曹楚南.钢筋在混凝土中腐蚀行为的电化学阻抗特征[J].腐蚀科学与防护技术,1999(03):161-164. |
| [10] | 杜雅莉,张俊喜,蒋俊,原徐杰,王灵芝,马行驰.C（l）-浓度渐变的混凝土孔隙液中钢筋的腐蚀过程[J].中国腐蚀与防护学报,2013(04):331-338. |
| [11] | G. K. Glass;N. R. Buenfeld .The influence of chloride binding on the chloride induced corrosion risk in reinforced concrete[J].Corrosion Science,2000(2):329-344. |
| [12] | 吴群,刘玉,杜荣归,林昌健.氯离子对模拟混凝土孔溶液中钢筋钝性影响的电化学研究[J].金属学报,2008(03):346-350. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%