利用氧等离子体浸没离子注入技术对聚合物材料(PET)进行表面改性后接枝有机抗菌剂赋予PET薄膜抗菌性能.试验结果表明:PET薄膜表面接枝上的抗菌剂在改性表面呈针状分布.经氧等离子体处理后的PET薄膜表面水接触角从78°降低到33°.红外光谱显示PET薄膜表面的分子结构被破坏,苯环的对位氢发生取代反应,分子链中形成了C-O亲水基团.氧等离子体的注入时闻和注入电压均对抗菌持久性有重要的影响,较高的注入电压能够使PET薄膜表面获得较深的改性层,利于改性表面亲水性的保持.注入时间超过10 min,电压超过-10 kV的样品在空气中放置40天后的抗菌率仍能达到90%以上.
Poly(ethyleneterephthalate)(PET)film was treated by oxygen plasma immersion ion implantation (O2-PIII),then grafted with triclosan to achieve the antibacterial surface properties.The treated surface was characterized by SEM,FTIR,and contact angle measurements.The antibacterial properties were evaluated utilizing the method of plate-counting of Escherichia coli(Gram negative).Results indicate that the surface of O2-PIII PET is more hydrophilic,and the modified film is grafted firmly with the antibacterial reagents.The changes in the surface hydrophicity may be attributed to that a large amount of oxygen is incorporated onto the surface.and C-C and C-H groups are changed into C-O groups by oxygen plasma immersion ion implantation.The plasma implantation time and bias voltage have critical influences on the perdurability of antibacterial efficacy.Higher implantation voltage leads to deeper modified layer of PET film,which is beneficial for long-term wettability of the modified surface of PET film.The antibacterial effect of the samples treated by -10 kV for more than 10 min still maintains above 90%after aging for 40 days in the air.
参考文献
| [1] | 周理水.PET塑料的改性及应用[J].塑料,2000(05):41-45. |
| [2] | 蔡明池.塑料包装材料现状与发展趋势[J].中国包装,2004(06):27-31. |
| [3] | Inagaki N.;Tasaka S.;Narushima K.;Kobayashi H. .Surface modification of PET films by pulsed argon plasma[J].Journal of Applied Polymer Science,2002(14):2845-2852. |
| [4] | 王进,潘长江,李鹏,孙鸿,黄楠.涤纶材料表面类金刚石薄膜的沉积及其抗菌性能研究[J].功能材料,2004(05):563-565. |
| [5] | Bhat NV.;Upadhyay DJ. .Plasma-induced surface modification and adhesion enhancement of polypropylene surface[J].Journal of Applied Polymer Science,2002(4):925-936. |
| [6] | 陈俊,刘正英,黄锐,殷茜,唐翌.PET改性研究进展[J].中国塑料,2003(06):20-25. |
| [7] | 方志,邱毓昌,罗毅.聚对苯二甲酸乙二酯薄膜表面亲水性的研究[J].绝缘材料,2004(03):26-28. |
| [8] | Cui NY.;Brown NMD. .Modification of the surface properties of a polypropylene (PP) film using an air dielectric barrier discharge plasma[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2002(1/2):31-38. |
| [9] | P. K. Chu;B. Y. Tang;L. P. Wang;X. F. Wang;S. Y. Wang;N. Huang .Third-generation plasma immersion ion implanter for biomedical materials and research[J].Review of Scientific Instruments,2001(3):1660-1665. |
| [10] | 董晓旭.抗菌高分子材料抗菌性检验方法的研究[J].工程塑料应用,2000(02):27-29. |
| [11] | 张晓林,马晓光.低温等离子体在PET膜接枝AM中的应用研究[J].印染,2005(14):15-18. |
| [12] | 陈建梅.红外光谱法对未知纤维的剖析[J].合成技术及应用,2003(02):47-49. |
| [13] | 朱红,李虎林,欧泽深,吕小丽,王淀佐.不同煤阶煤表面改性的FTIR谱研究[J].中国矿业大学学报,2001(04):366-370. |
| [14] | Zhang W;Chu PK;Ji JH;Zhang YH;Liu XY;Fu RKY;Ha PCT;Yan Q .Plasma surface modification of poly vinyl chloride for improvement of antibacterial properties[J].Biomaterials,2006(1):44-51. |
| [15] | 牛家嵘,顾振亚.利用低温空气等离子体改善聚酯和聚乙烯薄膜表面亲水性的研究[J].天津工业大学学报,2004(04):40-43,47. |
| [16] | 萧耀南,曾汉民,陈凤婷,张菊梅,郭伟鹏,吴清平.接枝型抗菌合成纤维的制备、结构与性能[J].高科技纤维与应用,2001(06):20-26. |
| [17] | Park JS.;Nho YC.;Kwon OH.;Kim JH. .Antibacterial activities of acrylic acid-grafted polypropylene fabric and its metallic salt[J].Journal of Applied Polymer Science,1998(11):2213-2220. |
| [18] | Cui NY.;Brown NMD. .Modification of the surface properties of a polypropylene (PP) film using an air dielectric barrier discharge plasma[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2002(1/2):31-38. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%