The sulfidation behavior of a 200 mum thick Fe-40at.%Al sheet has been investigated at temperatures between 973 K and 1273 K in H-2-H2S mixtures with H,S contents of 0.052-9.7vol%. The Fe-40Al sheet exhibited excellent sulfidation resistance at temperatures below 1073 K in all the H2S-H-2 mixtures. This may be attributed to the formation of a thin alumina film on the surface of the Fe-40Al sheet during sulfidation, identified by AES analysis. At temperatures higher than 1173 K, the Fe-40Al sheet also exhibited good sulfidation resistance in the 0.052%H2S-H-2, mixture. and there was only a slight increase in mass gain with tempe rat Lire. This compares favorably with Fe-200-11Al (in at.%) foil which was severely sulfidized even at 973 K in the 0.052% H2S-H-2 mixture, and showed markedly increased mass gain with increased H2S content and temperature. (C) 2004 Elsevier Ltd. All rights reserved.